Mixed moderate thermophilic bioleaching of Cu, Mo and Re from molybdenite concentrate: effects of silver ion, medium and energy sources
This study evaluates the effects of different additives such as silver ion, medium and energy sources on the efficiency of mixed moderate thermophilic bioleaching approach to extract Cu, Mo and Re from molybdenite concentrate containing 0.98% Cu, 1.56% Fe, 53.84% Mo, and 0.055% Re. Molybdenite was the major phase of Mo-bearing mineral and chalcopyrite, covellite and pyrite were distinguished as minor phases. The higher copper extraction was obtained in tests with silver additives in all types and quantities rather than tests without silver ion. Kinetic of copper dissolution varied in these experiments and depended on the types and amounts of silver, and other supplemented additives such as ferric ion. There was no clear difference in the copper extraction by various culture media and 100% of Cu was dissolved after 30 days of treatment, using 50 mg/L of silver nitrate as additives. In the best condition and without silver additives, maximum 60% of copper was extracted even in the presence of energy sources such as sulfur, ferrous and ferric ions. In the most effective test with initial pH 1.57, 50 mg/L silver nitrate, and 50 g/L ferric sulfate, 100% of copper was dissolved in less than a week with highest kinetics rate. Molybdenum and rhenium extraction had the same tends with redox potential graph. By increasing the redox potential to the 550-600mV, molybdenite started to dissolve and finally, molybdenum and rhenium were extracted 2% and 9.53% in the best condition; respectively.
Mixed moderate thermophilic bioleaching of Cu, Mo and Re from molybdenite concentrate: effects of silver ion, medium and energy sources
This study evaluates the effects of different additives such as silver ion, medium and energy sources on the efficiency of mixed moderate thermophilic bioleaching approach to extract Cu, Mo and Re from molybdenite concentrate containing 0.98% Cu, 1.56% Fe, 53.84% Mo, and 0.055% Re. Molybdenite was the major phase of Mo-bearing mineral and chalcopyrite, covellite and pyrite were distinguished as minor phases. The higher copper extraction was obtained in tests with silver additives in all types and quantities rather than tests without silver ion. Kinetic of copper dissolution varied in these experiments and depended on the types and amounts of silver, and other supplemented additives such as ferric ion. There was no clear difference in the copper extraction by various culture media and 100% of Cu was dissolved after 30 days of treatment, using 50 mg/L of silver nitrate as additives. In the best condition and without silver additives, maximum 60% of copper was extracted even in the presence of energy sources such as sulfur, ferrous and ferric ions. In the most effective test with initial pH 1.57, 50 mg/L silver nitrate, and 50 g/L ferric sulfate, 100% of copper was dissolved in less than a week with highest kinetics rate. Molybdenum and rhenium extraction had the same tends with redox potential graph. By increasing the redox potential to the 550-600mV, molybdenite started to dissolve and finally, molybdenum and rhenium were extracted 2% and 9.53% in the best condition; respectively.
Mixed moderate thermophilic bioleaching of Cu, Mo and Re from molybdenite concentrate: effects of silver ion, medium and energy sources
Hadi Abdollahi (Autor:in) / Sied Ziaeddin Shafaei (Autor:in) / Mohammad Noaparast (Autor:in) / Zahra Manafi (Autor:in)
2017
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
Metadata by DOAJ is licensed under CC BY-SA 1.0
Intensified bioleaching of low-grade molybdenite concentrate by ferrous sulfate and pyrite
| British Library Online Contents | 2015
Freeze-dry cryoprotectants of moderate thermophilic bacteria for bioleaching
| British Library Online Contents | 2008
Current and Future Development of Molybdenite Bioleaching Process
| British Library Online Contents | 2008
Bioleaching of marmatite concentrate in magnetic stirring reactor
| British Library Online Contents | 2005
Kinetics of the Oxidative Roasting of Low Grade Mongolian Molybdenite Concentrate
| British Library Online Contents | 2009