Der Einfluss des Molybdaengehaltes auf die Zeitstandfestigkeit niedriglegierter warmfester Staehle
Effect of molybdenum content on creep behavior at 450 to 600 C of low alloy heat resisting steels was investigated on four compositions of nominally 0.12% C, 0.5% Cr, 0.25% V, and 0, 0.25, 0.5, and 1% Mo; exposure times were maximum 20,000 hr; it was found that at 550 C, amounts to 0.5% Mo have favorable effect; at 575 C maximum beneficial effect is reached at 0.25% Mo.
Der Einfluss des Molybdaengehaltes auf die Zeitstandfestigkeit niedriglegierter warmfester Staehle
Effect of molybdenum content on creep behavior at 450 to 600 C of low alloy heat resisting steels was investigated on four compositions of nominally 0.12% C, 0.5% Cr, 0.25% V, and 0, 0.25, 0.5, and 1% Mo; exposure times were maximum 20,000 hr; it was found that at 550 C, amounts to 0.5% Mo have favorable effect; at 575 C maximum beneficial effect is reached at 0.25% Mo.
Der Einfluss des Molybdaengehaltes auf die Zeitstandfestigkeit niedriglegierter warmfester Staehle
Der Einfluss des Molybdaengehaltes auf die Zeitstandfestigkeit niedriglegierter warmfester Staehle
Foldyna, V. (Autor:in) / Prnka, T. (Autor:in)
Neue Huette ; 9
1964
5 pages
Aufsatz (Zeitschrift)
Deutsch
© Metadata Copyright Elsevier B. V. All rights reserved.
Die Entwicklung niedriglegierter Staehle fuer Baukonstruktionen
| Tema Archiv | 1972
Schweißen unlegierter und niedriglegierter Baustähle
| UB Braunschweig | 1980
Schweißen unlegierter und niedriglegierter Baustähle
| TIBKAT | 1980