Microstructure and mechanical properties of rheo-squeeze casting AZ91-Ca magnesium alloy prepared by gas bubbling process
Highlights Increase of gas flow led to improvement of the quality of AZX912 semi-solid slurry. Increase of gas flow improved ductility of rheo-squeeze casting AZX912 alloy. Increase of applied pressure led to refinement in as-cast microstructure. Increase of applied pressure improved both tensile strength and ductility. Heat treatment brought microstructure modification and increase of ductility.
Abstract Rheo-squeeze casting combined with gas bubbling process was proved effective to improve the mechanical properties of AZ91-2wt%Ca (AZX912) alloy. Increase of gas flow led to improvement of the quality of AZX912 semi-solid slurry and improved ductility of rheo-squeeze casting AZX912 alloy samples. Increase of applied pressure brought refinement in as-cast microstructure and reduction of porosity, as well as continuous improvement in both tensile strength and elongation. Heat treatment at 410°C promoted dissolution of β-Mg17Al12 phase, morphology modification of Al2Ca phase and further increase of both tensile strength and ductility. Compared with conventional squeeze casting, the mechanical properties of rheo-squeeze casting AZX912 alloy were improved by more than 20%. The improvement in mechanical properties was mainly attributed to the grain refinement in microstructure.
Microstructure and mechanical properties of rheo-squeeze casting AZ91-Ca magnesium alloy prepared by gas bubbling process
Highlights Increase of gas flow led to improvement of the quality of AZX912 semi-solid slurry. Increase of gas flow improved ductility of rheo-squeeze casting AZX912 alloy. Increase of applied pressure led to refinement in as-cast microstructure. Increase of applied pressure improved both tensile strength and ductility. Heat treatment brought microstructure modification and increase of ductility.
Abstract Rheo-squeeze casting combined with gas bubbling process was proved effective to improve the mechanical properties of AZ91-2wt%Ca (AZX912) alloy. Increase of gas flow led to improvement of the quality of AZX912 semi-solid slurry and improved ductility of rheo-squeeze casting AZX912 alloy samples. Increase of applied pressure brought refinement in as-cast microstructure and reduction of porosity, as well as continuous improvement in both tensile strength and elongation. Heat treatment at 410°C promoted dissolution of β-Mg17Al12 phase, morphology modification of Al2Ca phase and further increase of both tensile strength and ductility. Compared with conventional squeeze casting, the mechanical properties of rheo-squeeze casting AZX912 alloy were improved by more than 20%. The improvement in mechanical properties was mainly attributed to the grain refinement in microstructure.
Microstructure and mechanical properties of rheo-squeeze casting AZ91-Ca magnesium alloy prepared by gas bubbling process
Zhang, Yang (Autor:in) / Wu, Guohua (Autor:in) / Liu, Wencai (Autor:in) / Zhang, Liang (Autor:in) / Pang, Song (Autor:in) / Ding, Wenjiang (Autor:in)
31.10.2014
8 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
| British Library Online Contents | 2012
| British Library Online Contents | 2005
Microstructure and mechanical properties of rheo-diecast AZ91D magnesium alloy
| British Library Online Contents | 2006
Microstructure and Mechanical Properties of Ultrafine-Grained Magnesium AZ91 Alloy
| British Library Online Contents | 2014
Microstructure and Mechanical Behavior of Squeeze Cast SiC~w/AZ91 Magnesium Matrix Composites
| British Library Online Contents | 2001