Chemical shrinkage of portland cement pastes

Geiker, Mette / Knudsen, Torben

AbstractChemical shrinkage of normal Portland cement pastes (0.4 ≤ w/c < 0.8) has been measured at 20°C and of pastes with w/c = 0.5 furthermore at 35, and 50°C by means of measuring the volume change of samples of cement paste during the hydration. A small increase in the chemical shrinkage at “infinite time” was found at increasing water-cement ratio. The influence of the temperature was found to be twofold: Increasing temperature caused an increasing rate of the development of chemical shrinkage and a decrease of the chemical shrinkage at “infinite time”.Earlier studies of chemical shrinkage of Portland cement paste are also reported.

RésuméLe retrait chimique de la pâte de ciment de Portland normale (0.4 ≤ e/c < 0.8) a été mesuré à 20°C et les pâtes de e/c = 0.5également à 35°C et à 50°C en mesurent le changement de volume des échantillons de la pâte de ciment sous l'hydratation. Nous avons trouvé une légère augmentation du retrait chimique à l'infini lorsque le chiffre eau-ciment augmente. L'influence de la temperature a été trouvé double: une température en hausse implique une accélération du développement du retrait chimique et une réduction du retrait chimique a l'infini.Une résumé des enquêtes antérieures de retrait chimique de la pâte de ciment de Portland est également à trouver.