The effects of nanosilica on the fresh and hardened properties of 3D printable mortars

Sikora, Pawel / Chung, Sang-Yeop / Liard, Maxime / Lootens, Didier / Dorn, Tobias / Kamm, Paul H. / Stephan, Dietmar / Abd Elrahman, Mohamed

Abstract

Highlights • 3D printable mortars containing different dosages of nanosilica (NS) were developed and evaluated. • NS accelerates significantly the setting and hardening of printable mortar, while reducing its open time. • Increment of yield stress, together with an increment in NS dosage, was found to have occurred. • Optimal NS dosage results in improvement of the compressive strength and pore structure. • Incorporation of NS in the mixture resulted in improved buildability and decrement in pore anisotropy.

Abstract This study presents the experimental results of an investigation on the effects of nanosilica (NS) on the material characteristics of printable mortars used for additive manufacturing. Printable cement mortars based on Ordinary Portland Cement, limestone filler and silica sand were modified with different dosages of nanosilica (from 2% to 6% by weight of binder) and its influence on their hydration, rheological, mechanical and transport properties was assessed. The study showed that NS accelerates significantly the setting and hardening of printable mortar, while reducing its open time. Moreover, an increment of yield stress, together with an increment in NS dosage, was found to have occurred. The incorporation of an optimal NS dosage results in a noticeable increase in the compressive strength and alteration of the pore structure as determined by the MIP measurements. Moreover, transport properties of the produced mortar are significantly improved due to incorporation of NS. In addition to the microstructure refinement, Micro-CT and scanning electron microscopy (SEM) studies revealed that 3D printed mortars exhibit pore anisotropy in accordance with the printing direction. However, incorporation of NS in the mixture resulted in improved buildability, thus decreasing pore anisotropy.