The effects of ultrasonic peening treatment on the ultra-long life fatigue behavior of welded joints
AbstractThe conventional fatigue design codes was formulated based on the data from test stress cycles less than 1×107. Most of them could not be applied for welded structures serviced in the ultra-long life region so the new recommendations were discussed. The method of ultrasonic peening treatment (UPT) was introduced in this thesis as a post-weld treatment to improve the fatigue strength of the welded structures. The fatigue behavior of welded structures in the ultra-long life region was investigated using an ultrasonic fatigue test machine under two post-weld treatment states: the as-welded and the UPT. Discussion had also been made about the fracture mechanism on the UPT joints in ultra-long life fatigue test.
The effects of ultrasonic peening treatment on the ultra-long life fatigue behavior of welded joints
AbstractThe conventional fatigue design codes was formulated based on the data from test stress cycles less than 1×107. Most of them could not be applied for welded structures serviced in the ultra-long life region so the new recommendations were discussed. The method of ultrasonic peening treatment (UPT) was introduced in this thesis as a post-weld treatment to improve the fatigue strength of the welded structures. The fatigue behavior of welded structures in the ultra-long life region was investigated using an ultrasonic fatigue test machine under two post-weld treatment states: the as-welded and the UPT. Discussion had also been made about the fracture mechanism on the UPT joints in ultra-long life fatigue test.
The effects of ultrasonic peening treatment on the ultra-long life fatigue behavior of welded joints
Yin, Danqing (Autor:in) / Wang, Dongpo (Autor:in) / Jing, Hongyang (Autor:in) / Huo, Lixing (Autor:in)
04.02.2010
9 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
The effects of ultrasonic peening treatment on the ultra-long life fatigue behavior of welded joints
| British Library Online Contents | 2010
Discussion on fatigue design of welded joints enhanced by ultrasonic peening treatment (UPT)
| British Library Online Contents | 2009
Investigation on Improving Fatigue Properties of Welded Joints by Ultrasonic Peening Method
| British Library Online Contents | 2000
Analysis of the S-N curves of welded joints enhanced by ultrasonic peening treatment
| British Library Online Contents | 2011
Fatigue behaviour of welded joints with cracks, repaired by hammer peening
| Tema Archiv | 2004