Characterization of alkali silica reaction gels using Raman spectroscopy
AbstractThe ability of Raman spectroscopy to characterize amorphous materials makes this technique ideal to study alkali silica reaction (ASR) gels. The structure of several synthetic ASR gels was thoroughly characterized using Raman Spectroscopy. The results were validated with additional techniques such as Fourier transmission infrared spectroscopy, X-ray powder diffraction and thermogravimetric analysis. The Raman spectra were found to have two broad bands in the 800 to 1200cm−1 range and the 400 to 700cm−1 range indicating the amorphous nature of the gel. Important information regarding the silicate polymerization was deduced from both of these spectral regions. An increase in alkali content of the gels caused a depolymerization in the silicate framework which manifested in the Raman spectra as a gradual shift of predominant peaks in both regions. The trends in silicate depolymerization were in agreement with results from a NMR spectroscopy study on similar synthetic ASR gels.
Characterization of alkali silica reaction gels using Raman spectroscopy
AbstractThe ability of Raman spectroscopy to characterize amorphous materials makes this technique ideal to study alkali silica reaction (ASR) gels. The structure of several synthetic ASR gels was thoroughly characterized using Raman Spectroscopy. The results were validated with additional techniques such as Fourier transmission infrared spectroscopy, X-ray powder diffraction and thermogravimetric analysis. The Raman spectra were found to have two broad bands in the 800 to 1200cm−1 range and the 400 to 700cm−1 range indicating the amorphous nature of the gel. Important information regarding the silicate polymerization was deduced from both of these spectral regions. An increase in alkali content of the gels caused a depolymerization in the silicate framework which manifested in the Raman spectra as a gradual shift of predominant peaks in both regions. The trends in silicate depolymerization were in agreement with results from a NMR spectroscopy study on similar synthetic ASR gels.
Characterization of alkali silica reaction gels using Raman spectroscopy
Balachandran, C. (Autor:in) / Muñoz, J.F. (Autor:in) / Arnold, T. (Autor:in)
Cement and Concrete Research ; 92 ; 66-74
22.11.2016
9 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Characterization of alkali silica reaction gels using Raman spectroscopy
| Online Contents | 2017
Characterization of alkali silica reaction gels using Raman spectroscopy
| British Library Online Contents | 2017
Investigations on alkali-silica reaction products using Raman spectroscopy
| DOAJ | 2022
29Si MAS NMR Spectroscopic Investigation of Alkali Silica Reaction Product Gels
| Online Contents | 1993