Effects of welding parameters on friction stir spot welding of high density polyethylene sheets
Graphical abstract (a) Schematic illustration of the cross section of a friction stir spot weld and (b) Geometry of the weld bonded area, x: nugget thickness and y: the thickness of the upper sheet. Display Omitted Highlights ► Welding parameters affect the FSSW nugget formation and the strength of the joint. ► Melting of polyethylene occurred in the vicinity of the tool pin. ► The joint that fractures with a pull nugget failure mode has a higher strength.
Abstract Friction stir spot welding parameters affect the weld strength of thermoplastics, such as high density polyethylene (HDPE) sheets. The effects of the welding parameters on static strength of friction stir spot welds of high density polyethylene sheets were investigated. For maximizing the weld strength, the selection of welding parameters is very important. In lap-shear tests two fracture modes were observed; cross nugget failure and pull nugget failure. The tool rotational speed, tool plunge depth and dwell time were determined to be important in the joint formation and its strength. The joint which had a better strength fails with a pull nugget failure morphology. Weld cross section image analysis of the joints were done with a video spectral comparator. The plunge rate of the tool was determined to have a negligible effect on friction stir spot welding.
Effects of welding parameters on friction stir spot welding of high density polyethylene sheets
Graphical abstract (a) Schematic illustration of the cross section of a friction stir spot weld and (b) Geometry of the weld bonded area, x: nugget thickness and y: the thickness of the upper sheet. Display Omitted Highlights ► Welding parameters affect the FSSW nugget formation and the strength of the joint. ► Melting of polyethylene occurred in the vicinity of the tool pin. ► The joint that fractures with a pull nugget failure mode has a higher strength.
Abstract Friction stir spot welding parameters affect the weld strength of thermoplastics, such as high density polyethylene (HDPE) sheets. The effects of the welding parameters on static strength of friction stir spot welds of high density polyethylene sheets were investigated. For maximizing the weld strength, the selection of welding parameters is very important. In lap-shear tests two fracture modes were observed; cross nugget failure and pull nugget failure. The tool rotational speed, tool plunge depth and dwell time were determined to be important in the joint formation and its strength. The joint which had a better strength fails with a pull nugget failure morphology. Weld cross section image analysis of the joints were done with a video spectral comparator. The plunge rate of the tool was determined to have a negligible effect on friction stir spot welding.
Effects of welding parameters on friction stir spot welding of high density polyethylene sheets
Bilici, Mustafa Kemal (Autor:in) / Yukler, Ahmet Irfan (Autor:in)
29.04.2011
6 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Effects of welding parameters on friction stir spot welding of high density polyethylene sheets
British Library Online Contents | 2012
|British Library Online Contents | 2011
|