Assessment of long-term reactivity of initially lowly-reactive solid wastes as supplementary cementitious materials (SCMs)
Highlights A wide range of moderately to lowly reactive solid wastes as SCMs were explored. 180-Day relative strength had moderate correlation with R3 bound water content. 180-Day relative strength had moderate correlation with R3 portlandite consumption. 180-Day relative strength was adequately correlated with modified IS1727 results. Chapelle test results had a poor correlation with 180-day relative strengths.
Abstract Recently, due to various reasons, the amount of commercial supplementary cementitious materials (SCMs) available for the concrete industry has depleted and hence a wide range of moderately to lowly active solid wastes are being considered as SCMs. However, using such wastes as SCMs needs an efficient and practical procedure to estimate their long-term reactivity. For this purpose, different mechanical and chemical testing schemes have been specified (e.g. Chapelle test, relative strengths, activity index, modified lime reactivity test, R3 method) to assess their reactivities. In this study, a wide range of solid wastes including incinerated bottom ash (IBA), different colored soda-lime glass powders, fluorescent lamp glass powder (FLGP) and pulverized fly ash (PFA) were tested to evaluate their reactivities. It was found that there were moderate correlations between 180-day relative strengths (RS180day) of standard mortars and the bound water content or portlandite consumption of the R3 method. Moreover, the mortar strength values of the modified lime reactivity test were adequately correlated with RS180day of the standard mortars. In comparison, the portlandite consumption values of the Chapelle test had a poor correlation with RS180day. In addition, the studied materials can be classified as lowly-reactive (IBA), moderately-reactive (MGP, BGP, WGP, GGP, BGP, FLGP) and highly-reactive (PFA) SCMs.
Assessment of long-term reactivity of initially lowly-reactive solid wastes as supplementary cementitious materials (SCMs)
Highlights A wide range of moderately to lowly reactive solid wastes as SCMs were explored. 180-Day relative strength had moderate correlation with R3 bound water content. 180-Day relative strength had moderate correlation with R3 portlandite consumption. 180-Day relative strength was adequately correlated with modified IS1727 results. Chapelle test results had a poor correlation with 180-day relative strengths.
Abstract Recently, due to various reasons, the amount of commercial supplementary cementitious materials (SCMs) available for the concrete industry has depleted and hence a wide range of moderately to lowly active solid wastes are being considered as SCMs. However, using such wastes as SCMs needs an efficient and practical procedure to estimate their long-term reactivity. For this purpose, different mechanical and chemical testing schemes have been specified (e.g. Chapelle test, relative strengths, activity index, modified lime reactivity test, R3 method) to assess their reactivities. In this study, a wide range of solid wastes including incinerated bottom ash (IBA), different colored soda-lime glass powders, fluorescent lamp glass powder (FLGP) and pulverized fly ash (PFA) were tested to evaluate their reactivities. It was found that there were moderate correlations between 180-day relative strengths (RS180day) of standard mortars and the bound water content or portlandite consumption of the R3 method. Moreover, the mortar strength values of the modified lime reactivity test were adequately correlated with RS180day of the standard mortars. In comparison, the portlandite consumption values of the Chapelle test had a poor correlation with RS180day. In addition, the studied materials can be classified as lowly-reactive (IBA), moderately-reactive (MGP, BGP, WGP, GGP, BGP, FLGP) and highly-reactive (PFA) SCMs.
Assessment of long-term reactivity of initially lowly-reactive solid wastes as supplementary cementitious materials (SCMs)
Ali, Hafiz Asad (Autor:in) / Xuan, Dongxing (Autor:in) / Poon, Chi Sun (Autor:in)
06.10.2019
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
METHOD FOR MANUFACTURING OF SUPPLEMENTARY CEMENTITIOUS MATERIALS (SCMS)
| Europäisches Patentamt | 2020
METHOD FOR MANUFACTURING OF SUPPLEMENTARY CEMENTITIOUS MATERIALS (SCMS)
| Europäisches Patentamt | 2016
SCM METHOD FOR MANUFACTURING OF SUPPLEMENTARY CEMENTITIOUS MATERIALS SCMS
Europäisches Patentamt | 2019
Hydration kinetics of portland cement containing supplementary cementitious materials (SCMs)
| British Library Conference Proceedings | 2005