Mechanical performance of 6082-T6 aluminum alloy columns under eccentric compression at elevated temperatures

Ma, HuiHuan / Hou, Quanchao / Jiang, Yuqi / Yu, Zhiwei

Abstract To study the stability of aluminum alloy columns (AACs) under an axial compressive load and a bending moment at high temperatures, 30 AACs under eccentric compression were tested in a high-temperature environment. All the specimens were H-shaped, and the material was 6082-T6 aluminum alloy. After the test, it was found that all the AACs suffered bending and torsional instability. ABAQUS software was used to establish a finite element (FE) model. The accuracy of the FE model was validated by comparing the experimental results with those of the FE model. A design formula for the stability capacity of AACs under eccentric compression at high temperatures was proposed. To study the reliability of the formula, 2520 FE models were established at five different temperatures with two different cross sections. The results showed that the formula for the stability bearing capacity of AACs under eccentric compression at high temperatures was safe and reliable. Finally, the test results were compared with the results obtained using a fitting formula and European standard EC9. The results of EC9 were found to be more conservative, while the results of the fitting formula were closer to the experimental data.

Highlights • 30 6082-T6 aluminum columns under eccentric compression were tested at high temperatures. • Capacity formula for aluminum columns under eccentric compression at high temperatures was proposed. • 2520 FE models were established at five different temperatures to verify the proposed formula. • The results of the fitting formula were closer to the experimental data compared with EC9.