Effect of low-calcium and high-magnesium ferronickel slag on the microstructure and micromechanical properties of alkali-activated blended ground granulated blast furnace slag
https://orcid.org/0000-0003-1864-2258
Highlights The micromechanical properties of different phases in FNS particles are revealed. The micromechanical property of N-A-S-H gel in AAFNS is studied. The effects of FNS and activator type on the microstructural characteristics of AASF are investigated.
Abstract In recent years, low-calcium and high-magnesium ferronickel slag (FNS) has been gradually used in the preparation of alkali-activated cements (AACs). An in-depth exploration of the microstructural characteristics is crucial for a thorough understanding and enhancement of the macroscopic behaviors of AACs. In this study, the microstructural composition and micromechanical properties of the alkali-activated ground granulated blast furnace slag (GGBS)-FNS cements (AASF) prepared with sodium silicate and sodium hydroxide as alkali activators were quantitatively studied. Backscattered electron image analysis (BSE-IA) and nanoindentation were selected to reveal the micromechanical properties of different phases in FNS particles and AASF pastes. The results show that the elastic modulus of sodium aluminosilicate hydrate (N-A-S-H) in alkali-activated FNS cement is about 17 GPa, which is similar to that of the gel phase in alkali-activated fly ash cement (AAFA) and alkali-activated metakaolin cement (AAMK), confirming that the micromechanical property of N-A-S-H gel is independent of the kind of precursor materials. The Ca/Si and Al/Si of the hydration products in AASF gradually decline as FNS is incorporated, whereas the Mg/Al steadily rises, increasing the elastic modulus of the inner hydration product (IP) phase in AASF. The reaction degree of GGBS is higher in the sodium silicate-activated AASF system, while more N-A-S-H gels are formed in the sodium hydroxide-activated AASF system. The incorporation of FNS is conducive to improving the reaction degree of GGBS, resulting in the increase of calcium silicoaluminate hydrate (C-A-S-H) content and a significant decrease in IP content in AASF.
Effect of low-calcium and high-magnesium ferronickel slag on the microstructure and micromechanical properties of alkali-activated blended ground granulated blast furnace slag
https://orcid.org/0000-0003-1864-2258
Highlights The micromechanical properties of different phases in FNS particles are revealed. The micromechanical property of N-A-S-H gel in AAFNS is studied. The effects of FNS and activator type on the microstructural characteristics of AASF are investigated.
Abstract In recent years, low-calcium and high-magnesium ferronickel slag (FNS) has been gradually used in the preparation of alkali-activated cements (AACs). An in-depth exploration of the microstructural characteristics is crucial for a thorough understanding and enhancement of the macroscopic behaviors of AACs. In this study, the microstructural composition and micromechanical properties of the alkali-activated ground granulated blast furnace slag (GGBS)-FNS cements (AASF) prepared with sodium silicate and sodium hydroxide as alkali activators were quantitatively studied. Backscattered electron image analysis (BSE-IA) and nanoindentation were selected to reveal the micromechanical properties of different phases in FNS particles and AASF pastes. The results show that the elastic modulus of sodium aluminosilicate hydrate (N-A-S-H) in alkali-activated FNS cement is about 17 GPa, which is similar to that of the gel phase in alkali-activated fly ash cement (AAFA) and alkali-activated metakaolin cement (AAMK), confirming that the micromechanical property of N-A-S-H gel is independent of the kind of precursor materials. The Ca/Si and Al/Si of the hydration products in AASF gradually decline as FNS is incorporated, whereas the Mg/Al steadily rises, increasing the elastic modulus of the inner hydration product (IP) phase in AASF. The reaction degree of GGBS is higher in the sodium silicate-activated AASF system, while more N-A-S-H gels are formed in the sodium hydroxide-activated AASF system. The incorporation of FNS is conducive to improving the reaction degree of GGBS, resulting in the increase of calcium silicoaluminate hydrate (C-A-S-H) content and a significant decrease in IP content in AASF.
Effect of low-calcium and high-magnesium ferronickel slag on the microstructure and micromechanical properties of alkali-activated blended ground granulated blast furnace slag
https://orcid.org/0000-0003-1864-2258
Highlights The micromechanical properties of different phases in FNS particles are revealed. The micromechanical property of N-A-S-H gel in AAFNS is studied. The effects of FNS and activator type on the microstructural characteristics of AASF are investigated.
Abstract In recent years, low-calcium and high-magnesium ferronickel slag (FNS) has been gradually used in the preparation of alkali-activated cements (AACs). An in-depth exploration of the microstructural characteristics is crucial for a thorough understanding and enhancement of the macroscopic behaviors of AACs. In this study, the microstructural composition and micromechanical properties of the alkali-activated ground granulated blast furnace slag (GGBS)-FNS cements (AASF) prepared with sodium silicate and sodium hydroxide as alkali activators were quantitatively studied. Backscattered electron image analysis (BSE-IA) and nanoindentation were selected to reveal the micromechanical properties of different phases in FNS particles and AASF pastes. The results show that the elastic modulus of sodium aluminosilicate hydrate (N-A-S-H) in alkali-activated FNS cement is about 17 GPa, which is similar to that of the gel phase in alkali-activated fly ash cement (AAFA) and alkali-activated metakaolin cement (AAMK), confirming that the micromechanical property of N-A-S-H gel is independent of the kind of precursor materials. The Ca/Si and Al/Si of the hydration products in AASF gradually decline as FNS is incorporated, whereas the Mg/Al steadily rises, increasing the elastic modulus of the inner hydration product (IP) phase in AASF. The reaction degree of GGBS is higher in the sodium silicate-activated AASF system, while more N-A-S-H gels are formed in the sodium hydroxide-activated AASF system. The incorporation of FNS is conducive to improving the reaction degree of GGBS, resulting in the increase of calcium silicoaluminate hydrate (C-A-S-H) content and a significant decrease in IP content in AASF.
Effect of low-calcium and high-magnesium ferronickel slag on the microstructure and micromechanical properties of alkali-activated blended ground granulated blast furnace slag
Cao, Ruilin (Autor:in) / Jia, Zijian (Autor:in) / Zhang, Shunquan (Autor:in) / Chen, Chun (Autor:in) / Gao, Yueyi (Autor:in) / Zhang, Yamei (Autor:in)
18.09.2023
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Properties of alkali-activated ground granulated blast furnace slag blended with ferronickel slag
| British Library Online Contents | 2018
Alkali-activated blast furnace ferronickel slag sprayed concrete
| Europäisches Patentamt | 2020
COMPLEXED SLAG FINE AGGREGATE COMPRISING FERRONICKEL FURNACE SLAG AND GRANULATED BLAST FURNACE SLAG
| Europäisches Patentamt | 2019
COMPLEXED SLAG FINE AGGREGATE COMPRISING FERRONICKEL FURNACE SLAG AND GRANULATED BLAST FURNACE SLAG
Europäisches Patentamt | 2019
Hydration of alkali-activated ground granulated blast furnace slag
| Tema Archiv | 2000