Non-autoclaved high strength cellular concrete from alkali activated slag
Highlights ► Cellular concrete was made from sodium silicate activated blast furnace slag. ► High temperature curing was done at 85°C for achieving a good strength compared to AAC. ► Pore structure was optimized by the proper amount of Al powder and sodium lauryl sulfate. ► Sodium silicate modulus was optimized for the best strength and pore structure. ► For reducing autoclave cost it can be replaced by AAC with this method.
Abstract In this study, the use of alkali activated slag (AAS) in place of usual cementitious materials in the production of autoclave aerated concrete (AAC) was studied. This substitution altered autoclave curing stage by steam curing in AAC production process. In this way, after mixing of AAS paste with aluminum powder, enough time was given to the mixture. The resultant green body was then cured at 70, 78 and 87°C. To achieve the best results, microscopic pore structure, compressive strength of the body and mini-slump of initial paste were studied. The results approved that AAC can be produced without autoclave by using AAS.
Non-autoclaved high strength cellular concrete from alkali activated slag
Highlights ► Cellular concrete was made from sodium silicate activated blast furnace slag. ► High temperature curing was done at 85°C for achieving a good strength compared to AAC. ► Pore structure was optimized by the proper amount of Al powder and sodium lauryl sulfate. ► Sodium silicate modulus was optimized for the best strength and pore structure. ► For reducing autoclave cost it can be replaced by AAC with this method.
Abstract In this study, the use of alkali activated slag (AAS) in place of usual cementitious materials in the production of autoclave aerated concrete (AAC) was studied. This substitution altered autoclave curing stage by steam curing in AAC production process. In this way, after mixing of AAS paste with aluminum powder, enough time was given to the mixture. The resultant green body was then cured at 70, 78 and 87°C. To achieve the best results, microscopic pore structure, compressive strength of the body and mini-slump of initial paste were studied. The results approved that AAC can be produced without autoclave by using AAS.
Non-autoclaved high strength cellular concrete from alkali activated slag
Esmaily, H. (Autor:in) / Nuranian, H. (Autor:in)
Construction and Building Materials ; 26 ; 200-206
13.06.2011
7 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Non-autoclaved high strength cellular concrete from alkali activated slag
| British Library Online Contents | 2012
Non-autoclaved high strength cellular concrete from alkali activated slag
| Online Contents | 2012
Development of Non-Autoclaved Aerated Concrete by Alkali Activated Phosphorus Slag
| British Library Conference Proceedings | 2011
| British Library Online Contents | 1992
A preliminary study of autoclaved alkali-activated slag blended with quartz powder
| British Library Online Contents | 2012