Prediction of elevated temperature fatigue crack growth rates in TI-6AL-4V alloy – neural network approach
AbstractThe results obtained from two experimental test programs (TP-1 and TP-2) were used to train neural networks to predict elevated temperature, fatigue crack growth rates in Ti-6Al-4V alloy. Two programs, TP-1 and TP-2, were conducted at room and elevated temperatures under high humidity and laboratory air environments, respectively. While elevated temperature effects were investigated in TP-2, stress ratio effects were studied in TP-1 using several stress ratios. Networks were trained using the elevated temperature data to predict the crack growth rates at a given stress intensity under different temperatures. The experimental and predicted fatigue crack growth rates showed a least squared error of 0.03. Thus, this approach was found to predict fatigue crack growth rates in Ti-6Al-4V alloy at elevated temperatures.
Prediction of elevated temperature fatigue crack growth rates in TI-6AL-4V alloy – neural network approach
AbstractThe results obtained from two experimental test programs (TP-1 and TP-2) were used to train neural networks to predict elevated temperature, fatigue crack growth rates in Ti-6Al-4V alloy. Two programs, TP-1 and TP-2, were conducted at room and elevated temperatures under high humidity and laboratory air environments, respectively. While elevated temperature effects were investigated in TP-2, stress ratio effects were studied in TP-1 using several stress ratios. Networks were trained using the elevated temperature data to predict the crack growth rates at a given stress intensity under different temperatures. The experimental and predicted fatigue crack growth rates showed a least squared error of 0.03. Thus, this approach was found to predict fatigue crack growth rates in Ti-6Al-4V alloy at elevated temperatures.
Prediction of elevated temperature fatigue crack growth rates in TI-6AL-4V alloy – neural network approach
Fotovati, A (Autor:in) / Goswami, T (Autor:in)
02.03.2004
8 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
| British Library Online Contents | 2004
A neural network approach to elevated temperature creep - fatigue life prediction
| British Library Online Contents | 1999
Prediction of fatigue crack growth rates based on crack blunting
| British Library Online Contents | 1994
Elevated temperature fatigue crack growth behavior of Ti-1100
| British Library Online Contents | 1994
Elevated temperature fatigue crack growth in alloy 718-Part I: Effects of mechanical variables
| British Library Online Contents | 1993