Module de deformation longitudinale des pates de ciment portland conservees dans l'eau
AbstractAs, considering compressive strength, cement pastes separate into two groups of different behaviour, nothing alike is noticeable when considering their elastic modulus.We explain that by the fact that, although having similar compressive strength, the two main components of pastes, gel and anhydrous portion, have much different elastic moduli; anhydrous part is at least three times stiffer than gel.A formula linking the modulus of the paste to the moduli and proportions of its components must give results close to those of the theoretical limit E V = EaVa + EgVg. This involves equal strain of all components.
RésuméAlors que vis-à-vis des leur résistance en compression les pâtes durcies se séparent en deux ensembles de comportements distincts, rien de semblable n'est décelable lorsqu'on considère l'évolution de leur module de déformation longitudinale.Nous expliquons ceci par le fait que, malgré des résistances en compression semblables, les deux constituants principaux des pâtes, le gel et le reliquat anhydre, présentent des modules de déformation notablement différents.La loi de mélange reliant le module de la pâte aux modules et proportions de ses constituants doit donner des résultats très proches de la limite théorique E V = EaVa + EgVg.
Module de deformation longitudinale des pates de ciment portland conservees dans l'eau
AbstractAs, considering compressive strength, cement pastes separate into two groups of different behaviour, nothing alike is noticeable when considering their elastic modulus.We explain that by the fact that, although having similar compressive strength, the two main components of pastes, gel and anhydrous portion, have much different elastic moduli; anhydrous part is at least three times stiffer than gel.A formula linking the modulus of the paste to the moduli and proportions of its components must give results close to those of the theoretical limit E V = EaVa + EgVg. This involves equal strain of all components.
RésuméAlors que vis-à-vis des leur résistance en compression les pâtes durcies se séparent en deux ensembles de comportements distincts, rien de semblable n'est décelable lorsqu'on considère l'évolution de leur module de déformation longitudinale.Nous expliquons ceci par le fait que, malgré des résistances en compression semblables, les deux constituants principaux des pâtes, le gel et le reliquat anhydre, présentent des modules de déformation notablement différents.La loi de mélange reliant le module de la pâte aux modules et proportions de ses constituants doit donner des résultats très proches de la limite théorique E V = EaVa + EgVg.
Module de deformation longitudinale des pates de ciment portland conservees dans l'eau
Granju, J.L. (Autor:in) / Maso, J.C. (Autor:in)
Cement and Concrete Research ; 10 ; 731-738
17.07.1980
8 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Französisch
Propagation du front de carbonatation dans les pates de ciment
| British Library Conference Proceedings | 1998
| Taylor & Francis Verlag | 2001
Liaisons Pâtes de ciment, matériaux associés : Colloque International ; Communications
| UB Braunschweig | 1982