Stress corrosion initiated cracking of concrete
AbstractThe simultaneous action of corrosive media and mechanical stresses on concrete leads to stress corrosion cracking phenomena. The flexural strength of mortar specimens in sulfate-solutions has been found to depend significantly on the external load being applied during the sulfate-solution exposure of the specimens. Low stresses cause a relatively higher specific decrease of flexural strength than higher stresses. The effects observed are of fundamental importance with respect to the evaluation of the durability of concrete structures subjected to corrosive media.
Stress corrosion initiated cracking of concrete
AbstractThe simultaneous action of corrosive media and mechanical stresses on concrete leads to stress corrosion cracking phenomena. The flexural strength of mortar specimens in sulfate-solutions has been found to depend significantly on the external load being applied during the sulfate-solution exposure of the specimens. Low stresses cause a relatively higher specific decrease of flexural strength than higher stresses. The effects observed are of fundamental importance with respect to the evaluation of the durability of concrete structures subjected to corrosive media.
Stress corrosion initiated cracking of concrete
Schneider, U. (Autor:in) / Nägele, E. (Autor:in) / Dumat, F. (Autor:in)
Cement and Concrete Research ; 16 ; 535-544
19.03.1986
10 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
A phase field model for simulating the stress corrosion cracking initiated from pits
| British Library Online Contents | 2017
| British Library Online Contents | 2014
A phase field model for simulating the stress corrosion cracking initiated from pits
| British Library Online Contents | 2017
Engineering Index Backfile | 1945