Preparation of poly(decaglycerol-co-ethylene glycol) copolymer as phase change material
Highlights ► This research provides a new shape-stabilized phase change material poly(decaglycerol-co-ethylene glycol) [P(DG-co-EG)] with higher crystallization enthalpy 141.3J/g. ► In this work, a new high activity cross-linked monomer PDGA with end-double bond was prepared and used. ► The soaking time of P(DG-co-EG) can reach to 15min at room temperature. ► P(DG-co-EG) has better thermal stability below 210°C.
Abstract In this work, a novel phase change material poly(decaglycerol-co-ethylene glycol) [P(DG-co-EG)] copolymer was prepared by free-radical solution polymerization based on two macromonomers, polyethylene glycol acrylate (PEGA) and polydecaglycerol acrylate (PDGA), which were synthesized via acryloyl chloride modification. The results showed that the crystallization enthalpy of P(DG-co-EG) achieved to 141.3J/g, and its soaking time increased up to 15min with the increase of molar ratios of PEGA to PDGA:TGA results indicated that P(DG-co-EG) degraded in two steps and its maximum degradation rate was at 420°C.
Preparation of poly(decaglycerol-co-ethylene glycol) copolymer as phase change material
Highlights ► This research provides a new shape-stabilized phase change material poly(decaglycerol-co-ethylene glycol) [P(DG-co-EG)] with higher crystallization enthalpy 141.3J/g. ► In this work, a new high activity cross-linked monomer PDGA with end-double bond was prepared and used. ► The soaking time of P(DG-co-EG) can reach to 15min at room temperature. ► P(DG-co-EG) has better thermal stability below 210°C.
Abstract In this work, a novel phase change material poly(decaglycerol-co-ethylene glycol) [P(DG-co-EG)] copolymer was prepared by free-radical solution polymerization based on two macromonomers, polyethylene glycol acrylate (PEGA) and polydecaglycerol acrylate (PDGA), which were synthesized via acryloyl chloride modification. The results showed that the crystallization enthalpy of P(DG-co-EG) achieved to 141.3J/g, and its soaking time increased up to 15min with the increase of molar ratios of PEGA to PDGA:TGA results indicated that P(DG-co-EG) degraded in two steps and its maximum degradation rate was at 420°C.
Preparation of poly(decaglycerol-co-ethylene glycol) copolymer as phase change material
Guo, Jing (Autor:in) / Xiang, Hengxue (Autor:in) / Wang, Qianqian (Autor:in) / Hu, Chengnv (Autor:in) / Zhu, Meifang (Autor:in) / Li, Lili (Autor:in)
Energy and Buildings ; 48 ; 206-210
28.01.2012
5 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Preparation of poly(decaglycerol-co-ethylene glycol) copolymer as phase change material
| Online Contents | 2012
Preparation of poly(decaglycerol-co-ethylene glycol) copolymer as phase change material
| Online Contents | 2011
| British Library Online Contents | 2006
| British Library Online Contents | 2007
Preparation of poly(ethylene glycol)-grafted alumina
| British Library Online Contents | 1993