Investigation on AISI 304 austenitic stainless steel to AISI 4140 low alloy steel dissimilar joints by gas tungsten arc, electron beam and friction welding
Research highlights ► Beneficial effects of FRW, GTAW and EBW joints of dissimilar AISI 304 and AISI 4140 materials. ► Comparative study of FRW, GTAW and EBW joints on mechanical properties. ► SEM/EDAX, XRD analysis on dissimilar AISI 304 and AISI 4140 materials.
Abstract This paper presents the investigations carried out to study the microstructure and mechanical properties of AISI 304 stainless steel and AISI 4140 low alloy steel joints by Gas Tungsten Arc Welding (GTAW), Electron Beam Welding (EBW) and Friction Welding (FRW). For each of the weldments, detailed analysis was conducted on the phase composition, microstructure characteristics and mechanical properties. The results of the analysis shows that the joint made by EBW has the highest tensile strength (681MPa) than the joint made by GTAW (635Mpa) and FRW (494Mpa). From the fractographs, it could be observed that the ductility of the EBW and GTA weldment were higher with an elongation of 32% and 25% respectively when compared with friction weldment (19%). Moreover, the impact strength of weldment made by GTAW is higher compared to EBW and FRW.
Investigation on AISI 304 austenitic stainless steel to AISI 4140 low alloy steel dissimilar joints by gas tungsten arc, electron beam and friction welding
Research highlights ► Beneficial effects of FRW, GTAW and EBW joints of dissimilar AISI 304 and AISI 4140 materials. ► Comparative study of FRW, GTAW and EBW joints on mechanical properties. ► SEM/EDAX, XRD analysis on dissimilar AISI 304 and AISI 4140 materials.
Abstract This paper presents the investigations carried out to study the microstructure and mechanical properties of AISI 304 stainless steel and AISI 4140 low alloy steel joints by Gas Tungsten Arc Welding (GTAW), Electron Beam Welding (EBW) and Friction Welding (FRW). For each of the weldments, detailed analysis was conducted on the phase composition, microstructure characteristics and mechanical properties. The results of the analysis shows that the joint made by EBW has the highest tensile strength (681MPa) than the joint made by GTAW (635Mpa) and FRW (494Mpa). From the fractographs, it could be observed that the ductility of the EBW and GTA weldment were higher with an elongation of 32% and 25% respectively when compared with friction weldment (19%). Moreover, the impact strength of weldment made by GTAW is higher compared to EBW and FRW.
Investigation on AISI 304 austenitic stainless steel to AISI 4140 low alloy steel dissimilar joints by gas tungsten arc, electron beam and friction welding
Arivazhagan, N. (Autor:in) / Singh, Surendra (Autor:in) / Prakash, Satya (Autor:in) / Reddy, G.M. (Autor:in)
24.01.2011
15 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
| British Library Online Contents | 2011
Dissimilar friction stir welding of AISI 430 ferritic and AISI 304L austenitic stainless steels
| Springer Verlag | 2020
Friction stir welding of AISI 304 austenitic stainless steel
| British Library Online Contents | 2007
Dissimilar friction stir welding of AISI 430 ferritic and AISI 304L austenitic stainless steels
| Springer Verlag | 2020
Characterization of Friction Welding for IN713LC and AISI 4140 Steel
| British Library Online Contents | 2004