Protection of reinforcement steel corrosion by phenylphosphonic acid pre-treatment PART II: Tests in mortar medium
Abstract A pre-treatment of steel reinforcement in mortar by a 72 h immersion in 0.1 M phenyl-phosphonic acid (C6H5P(O)(OH)2; PPA) was investigated. Then effectiveness of this procedure for protection against the corrosion of steel bars embedded in pre- or post-addition of sodium chloride mortar was evaluated by electrochemical impedance spectroscopy, visual inspection, SEM, and EDS analyses. The results showed that for non-treated steel reinforcement, the charge transfer resistance (R t) decreases considerably with time indicating a very advanced state of corrosion after 54 months corrosion test. In contrast, for pre-treated steel rebar, this resistance remains high reflecting the effectiveness of the pre-treatment method against corrosion. The corrosion rate evaluated from the charge transfer resistance at 54 months corrosion in chloride containing medium was 0.5 μm year−1.
Protection of reinforcement steel corrosion by phenylphosphonic acid pre-treatment PART II: Tests in mortar medium
Abstract A pre-treatment of steel reinforcement in mortar by a 72 h immersion in 0.1 M phenyl-phosphonic acid (C6H5P(O)(OH)2; PPA) was investigated. Then effectiveness of this procedure for protection against the corrosion of steel bars embedded in pre- or post-addition of sodium chloride mortar was evaluated by electrochemical impedance spectroscopy, visual inspection, SEM, and EDS analyses. The results showed that for non-treated steel reinforcement, the charge transfer resistance (R t) decreases considerably with time indicating a very advanced state of corrosion after 54 months corrosion test. In contrast, for pre-treated steel rebar, this resistance remains high reflecting the effectiveness of the pre-treatment method against corrosion. The corrosion rate evaluated from the charge transfer resistance at 54 months corrosion in chloride containing medium was 0.5 μm year−1.
Protection of reinforcement steel corrosion by phenylphosphonic acid pre-treatment PART II: Tests in mortar medium
Etteyeb, N. (Autor:in) / Dhouibi, L. (Autor:in) / Takenouti, H. (Autor:in) / Triki, E. (Autor:in)
Cement and Concrete Composites ; 65 ; 94-100
07.10.2015
7 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
| Taylor & Francis Verlag | 2022
The corrosion behaviour of polypyrrole coating synthesized in phenylphosphonic acid solution
| British Library Online Contents | 2006
Adsorption structure of phenylphosphonic acid on an alumina surface
| British Library Online Contents | 2009
Corrosion protection of steel in pumice lightweight mortar by coatings
| Online Contents | 2005