Age-hardening behavior of powder metallurgy AA2014 alloy
AbstractThe aim of this paper is to investigate age hardening behavior of PM AA2014 alloy. The specimens were made by powder metallurgy (PM) method. During the PM the product was made from powder basic materials by pressing (at 600MPa) and sintering (600±5°C, 610±5°C, 620±5°C). There were three steps that occur in age-hardening; solution treatment (510±5°C), quenching (water) and aging (20°C, 150±5°C, 200±5°C). Metal microscopy and micro Vickers hardness test were carried out to characterize the structure properties resulting from different aging temperature. The hardness test results showed that the sintering temperature, suitable solution treatment and aging operations has great influence on hardness characteristics of the PM alloys.
Age-hardening behavior of powder metallurgy AA2014 alloy
AbstractThe aim of this paper is to investigate age hardening behavior of PM AA2014 alloy. The specimens were made by powder metallurgy (PM) method. During the PM the product was made from powder basic materials by pressing (at 600MPa) and sintering (600±5°C, 610±5°C, 620±5°C). There were three steps that occur in age-hardening; solution treatment (510±5°C), quenching (water) and aging (20°C, 150±5°C, 200±5°C). Metal microscopy and micro Vickers hardness test were carried out to characterize the structure properties resulting from different aging temperature. The hardness test results showed that the sintering temperature, suitable solution treatment and aging operations has great influence on hardness characteristics of the PM alloys.
Age-hardening behavior of powder metallurgy AA2014 alloy
Durmuş, Hülya Kaçar (Autor:in) / Meriç, Cevdet (Autor:in)
30.11.2005
5 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Age-hardening behavior of powder metallurgy AA2014 alloy
| British Library Online Contents | 2007
Homogenization and Hot Workability of Alloy AA2014
| British Library Online Contents | 2002
Microstructure, mechanical properties and corrosion behavior of friction stir processed AA2014 alloy
| Springer Verlag | 2022
Salt fog corrosion behavior of friction stir welded AA2014-T651 aluminum alloy
| British Library Online Contents | 2016
Microstructure, mechanical properties and corrosion behavior of friction stir processed AA2014 alloy
| Springer Verlag | 2022