Dolomite used as raw material to produce MgO-based expansive agent
AbstractIn this paper, the manufacture of MgO-based expansive agent using dolomite as raw material was studied. The decomposition of dolomite was discussed at first by DTA-TG analysis and on the crystalline view. On the characteristics of decomposition of dolomite, the authors think it is possible to use dolomite as raw material, but the silica-bearing mineral is considered to combine the CaO released from dolomite to form silicate. The phases of MgO-based expansive agent are mainly MgO, C2S and a little amount of CaO. The expansion of resulting expansive agents by autoclaving testing and hot water curing at 80 °C shows that the MgO-based expansive agents have desired expansion. If the burning temperature and burning time, dosage in cement are controlled according to the requirement of concrete construction, the MgO-based expansive agent can be used to compensate the shrinkage as designed.
Dolomite used as raw material to produce MgO-based expansive agent
AbstractIn this paper, the manufacture of MgO-based expansive agent using dolomite as raw material was studied. The decomposition of dolomite was discussed at first by DTA-TG analysis and on the crystalline view. On the characteristics of decomposition of dolomite, the authors think it is possible to use dolomite as raw material, but the silica-bearing mineral is considered to combine the CaO released from dolomite to form silicate. The phases of MgO-based expansive agent are mainly MgO, C2S and a little amount of CaO. The expansion of resulting expansive agents by autoclaving testing and hot water curing at 80 °C shows that the MgO-based expansive agents have desired expansion. If the burning temperature and burning time, dosage in cement are controlled according to the requirement of concrete construction, the MgO-based expansive agent can be used to compensate the shrinkage as designed.
Dolomite used as raw material to produce MgO-based expansive agent
Lingling, Xu (Autor:in) / Min, Deng (Autor:in)
Cement and Concrete Research ; 35 ; 1480-1485
23.09.2004
6 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Dolomite used as raw material to produce MgO-based expansive agent
| Online Contents | 2005
Dolomite used as raw material to produce MgO-based expansive agent
| Tema Archiv | 2005
Dolomite used as raw material to produce MgO-based expansive agent
| British Library Online Contents | 2005
| British Library Online Contents | 2015