The anisotropy of laser melting deposition additive manufacturing Ti–6.5Al–3.5Mo–1.5Zr–0.3Si titanium alloy
https://orcid.org/0000-0002-3845-4150
Highlights As-deposited sample exhibits columnar morphology and strong tensile anisotropy. The α+β annealing do not change the grain morphology and the anisotropy. The columnar grains transform into equiaxed grains during β annealing. The β annealing substantially decreases the tensile anisotropy.
Abstract The anisotropy of laser melting deposition additive manufacturing Ti–6.5Al–3.5Mo–1.5Zr–0.3Si was studied by microstructure observation and room tensile properties testing. The as-deposited sample exhibits a strong tensile anisotropy due to the columnar grains morphology and the strong texture of β 〈001〉 parallel to the deposition direction. Annealing in the upper α+β region has little effect on the grain morphology and the anisotropy. However, annealing in the single β region transforms the grain morphology from columnar to equiaxed which substantially reduces the tensile anisotropy to a very low level.
The anisotropy of laser melting deposition additive manufacturing Ti–6.5Al–3.5Mo–1.5Zr–0.3Si titanium alloy
https://orcid.org/0000-0002-3845-4150
Highlights As-deposited sample exhibits columnar morphology and strong tensile anisotropy. The α+β annealing do not change the grain morphology and the anisotropy. The columnar grains transform into equiaxed grains during β annealing. The β annealing substantially decreases the tensile anisotropy.
Abstract The anisotropy of laser melting deposition additive manufacturing Ti–6.5Al–3.5Mo–1.5Zr–0.3Si was studied by microstructure observation and room tensile properties testing. The as-deposited sample exhibits a strong tensile anisotropy due to the columnar grains morphology and the strong texture of β 〈001〉 parallel to the deposition direction. Annealing in the upper α+β region has little effect on the grain morphology and the anisotropy. However, annealing in the single β region transforms the grain morphology from columnar to equiaxed which substantially reduces the tensile anisotropy to a very low level.
The anisotropy of laser melting deposition additive manufacturing Ti–6.5Al–3.5Mo–1.5Zr–0.3Si titanium alloy
https://orcid.org/0000-0002-3845-4150
Highlights As-deposited sample exhibits columnar morphology and strong tensile anisotropy. The α+β annealing do not change the grain morphology and the anisotropy. The columnar grains transform into equiaxed grains during β annealing. The β annealing substantially decreases the tensile anisotropy.
Abstract The anisotropy of laser melting deposition additive manufacturing Ti–6.5Al–3.5Mo–1.5Zr–0.3Si was studied by microstructure observation and room tensile properties testing. The as-deposited sample exhibits a strong tensile anisotropy due to the columnar grains morphology and the strong texture of β 〈001〉 parallel to the deposition direction. Annealing in the upper α+β region has little effect on the grain morphology and the anisotropy. However, annealing in the single β region transforms the grain morphology from columnar to equiaxed which substantially reduces the tensile anisotropy to a very low level.
The anisotropy of laser melting deposition additive manufacturing Ti–6.5Al–3.5Mo–1.5Zr–0.3Si titanium alloy
Zhu, Yanyan (Autor:in) / Tian, Xiangjun (Autor:in) / Li, Jia (Autor:in) / Wang, Huaming (Autor:in)
01.11.2014
5 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Characterization of Ti-6.5Al-3.5Mo-1.5Zr-0.3Si Titanium Alloy by Laser Shock Peening
| British Library Online Contents | 2012
| British Library Online Contents | 2014
| British Library Online Contents | 2014
Analysis on Finish Hard Turning of Ti-6.5Al-3.5Mo-1.5Zr-0.3Si Alloy
| British Library Online Contents | 2009
Fatigue crack growth behaviour in laser melting deposited Ti-6.5Al-3.5Mo-1.5Zr-0.3Si alloy
| British Library Online Contents | 2017