Microstructure and mechanical properties of ultrasonic spot welded Al/Ti alloy joints
Graphical abstract Display Omitted
Highlights USWed dissimilar joints between Al5754–O and Ti–6Al–4V alloys were studied. Significant difference in the microstructure was observed at interface of joints. An asymmetrical hardness profile across the dissimilar joint was observed. A sound joint was obtained.
Abstract The microstructure, hardness, and tensile properties of solid-state ultrasonic spot welded (USWed) dissimilar joints between Al5754–O and Ti–6Al–4V alloys with or without a pure Al interlayer were studied. Significant difference in the microstructure was observed at the interface of the USWed Al/Ti alloy joints, where the phenomenon of adhesion on each side of the joint with Al interlayer was more obvious than that of the joint without Al interlayer. An asymmetrical hardness profile across the dissimilar joint was observed such that the hardness value increased gradually from the Al side to the Ti side. With increasing energy input, the lap shear strength of the USWed Al/Ti alloy joint with a 75μm thick Al interlayer first increased and then decreased, with the maximum lap shear strength reaching about 206MPa at a welding energy of 1000J. No samples failed at the interface when the energy was above 1000J or the thickness of Al interlayer was more than 75μm. The fracture was predominantly characterized by the dimple-like ductile fracture.
Microstructure and mechanical properties of ultrasonic spot welded Al/Ti alloy joints
Graphical abstract Display Omitted
Highlights USWed dissimilar joints between Al5754–O and Ti–6Al–4V alloys were studied. Significant difference in the microstructure was observed at interface of joints. An asymmetrical hardness profile across the dissimilar joint was observed. A sound joint was obtained.
Abstract The microstructure, hardness, and tensile properties of solid-state ultrasonic spot welded (USWed) dissimilar joints between Al5754–O and Ti–6Al–4V alloys with or without a pure Al interlayer were studied. Significant difference in the microstructure was observed at the interface of the USWed Al/Ti alloy joints, where the phenomenon of adhesion on each side of the joint with Al interlayer was more obvious than that of the joint without Al interlayer. An asymmetrical hardness profile across the dissimilar joint was observed such that the hardness value increased gradually from the Al side to the Ti side. With increasing energy input, the lap shear strength of the USWed Al/Ti alloy joint with a 75μm thick Al interlayer first increased and then decreased, with the maximum lap shear strength reaching about 206MPa at a welding energy of 1000J. No samples failed at the interface when the energy was above 1000J or the thickness of Al interlayer was more than 75μm. The fracture was predominantly characterized by the dimple-like ductile fracture.
Microstructure and mechanical properties of ultrasonic spot welded Al/Ti alloy joints
Wang, S.Q. (Autor:in) / Patel, V.K. (Autor:in) / Bhole, S.D. (Autor:in) / Wen, G.D. (Autor:in) / Chen, D.L. (Autor:in)
13.04.2015
9 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Fatigue life estimation of ultrasonic spot welded Mg alloy joints
| British Library Online Contents | 2014
Fatigue life estimation of ultrasonic spot welded Mg alloy joints
| Elsevier | 2014
| British Library Online Contents | 2016
Microstructures and mechanical properties of resistance spot welded magnesium alloy joints
| British Library Online Contents | 2007
| British Library Online Contents | 2016