Fatigue testing of butt-welded high strength square hollow sections strengthened with CFRP
AbstractThis paper presents a study on the residual stress, hardness and fatigue behaviour of butt-welded high strength square hollow section (SHS) steel tubes strengthened with carbon fibre reinforced polymer (CFRP). SHS tubes, with a nominal yield stress of 780MPa and an ultimate tensile strength of 860MPa, were butt-welded using the Gas Tungsten Arc Welding (GTAW) welding method. The hardness in the heat affected zone (HAZ) dropped to around 80% of that of the parent metal of the SHS steel. The strength in HAZ of the butt-welded SHS tubes is about 93% of that of the parent metal of the SHS tube. The residual stress of the butt-welded SHS tubes is about 20–50% 25-45%of the yield stress along the longitudinal direction and 15% of the yield stress along the transverse direction. The fatigue life of CFRP strengthened butt-welded SHS beams was extended for about 5 times comparing to the butt-welded beams without CFRP strengthening.
HighlightsMeasured residual stress and hardness of butt-welded high strength square hollow section (SHS).Examined microstructure of heat-affected zone (HAZ) in welded high strength SHS.Conducted fatigue tests on welded high strength SHS with and without CFRP strengthening.CFRP strengthening increased fatigue life about 5 times.
Fatigue testing of butt-welded high strength square hollow sections strengthened with CFRP
AbstractThis paper presents a study on the residual stress, hardness and fatigue behaviour of butt-welded high strength square hollow section (SHS) steel tubes strengthened with carbon fibre reinforced polymer (CFRP). SHS tubes, with a nominal yield stress of 780MPa and an ultimate tensile strength of 860MPa, were butt-welded using the Gas Tungsten Arc Welding (GTAW) welding method. The hardness in the heat affected zone (HAZ) dropped to around 80% of that of the parent metal of the SHS steel. The strength in HAZ of the butt-welded SHS tubes is about 93% of that of the parent metal of the SHS tube. The residual stress of the butt-welded SHS tubes is about 20–50% 25-45%of the yield stress along the longitudinal direction and 15% of the yield stress along the transverse direction. The fatigue life of CFRP strengthened butt-welded SHS beams was extended for about 5 times comparing to the butt-welded beams without CFRP strengthening.
HighlightsMeasured residual stress and hardness of butt-welded high strength square hollow section (SHS).Examined microstructure of heat-affected zone (HAZ) in welded high strength SHS.Conducted fatigue tests on welded high strength SHS with and without CFRP strengthening.CFRP strengthening increased fatigue life about 5 times.
Fatigue testing of butt-welded high strength square hollow sections strengthened with CFRP
Amraei, Mohsen (Autor:in) / Jiao, Hui (Autor:in) / Zhao, Xiao-Ling (Autor:in) / Tong, Le-Wei (Autor:in)
Thin-Walled Structures ; 120 ; 260-268
05.09.2017
9 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
CFRP strengthened butt-welded very high strength (VHS) circular steel tubes
| Online Contents | 2004
Simulation of CFRP strengthened butt-welded Very High Strength (VHS) circular steel tubes in tension
| British Library Conference Proceedings | 2009
Fatigue strength of CFRP strengthened welded joints with corrugated steel plates
| British Library Online Contents | 2015