Investigations on the structure of fully hydrated portland cement and tricalcium silicate pastes. II. Total porosity and pore size distribution
AbstractOn a series of OPC pastes hydrated at 20 °C and 90 °C and Ca3SiO5 pastes hydrated at 20 °C the total porosity and pore size distribution were measured. Data obtained by mercury porosimetry and nitrogen adsorption did not agree well as the volumina of pores filled with Hg and N2 differed. Regardless on the method employed the found pore size distribution depended on the starting water-solid ratio; as equal porosity, it was different in different hydrated materials.
Investigations on the structure of fully hydrated portland cement and tricalcium silicate pastes. II. Total porosity and pore size distribution
AbstractOn a series of OPC pastes hydrated at 20 °C and 90 °C and Ca3SiO5 pastes hydrated at 20 °C the total porosity and pore size distribution were measured. Data obtained by mercury porosimetry and nitrogen adsorption did not agree well as the volumina of pores filled with Hg and N2 differed. Regardless on the method employed the found pore size distribution depended on the starting water-solid ratio; as equal porosity, it was different in different hydrated materials.
Investigations on the structure of fully hydrated portland cement and tricalcium silicate pastes. II. Total porosity and pore size distribution
Odler, I. (Autor:in) / Köster, H. (Autor:in)
Cement and Concrete Research ; 16 ; 893-901
18.07.1986
9 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Investigations on the Aging of Hydrated Tricalcium Silicate and Portland Cement Pastes
| British Library Online Contents | 1995
Investigations on the Aging of Hydrated Tricalcium Silicate and Portland Cement Pastes
| Online Contents | 1995
Elastic moduli of hardened portland cement and tricalcium silicate pastes -- Effect of porosity
| Engineering Index Backfile | 1966