Rotating bending fatigue properties of two case hardening steels after nitriding treatment
Highlights ► Rotating bending fatigue tests have been conducted for Al-containing nitrided steels. ► Nitriding can remarkably increase the fatigue limits of the steels. ► After nitriding, the crack initiation sites have moved from the surface into subsurface. ► The steel with a lower [N] content has a higher fatigue limit.
Abstract Fatigue properties of two Al-containing steels have been investigated by rotating bending fatigue tests. Results show that the fatigue limits (the fatigue strength at 107 cycles) were improved remarkably by plasma nitriding due to the high hardness of 1000Hv and compressive stress of 400MPa in the nitrided layer. Scanning electron microscopic observations show that after nitriding the fatigue crack initiation sites moved from the surface flaws or near-surface matrix into the AlN inclusions at around the case-core interface. Degassing treatment can increase the fatigue limit because it prevented fatigue crack initiation at AlN inclusions due to the reduced [N] contents and refined inclusion size.
Rotating bending fatigue properties of two case hardening steels after nitriding treatment
Highlights ► Rotating bending fatigue tests have been conducted for Al-containing nitrided steels. ► Nitriding can remarkably increase the fatigue limits of the steels. ► After nitriding, the crack initiation sites have moved from the surface into subsurface. ► The steel with a lower [N] content has a higher fatigue limit.
Abstract Fatigue properties of two Al-containing steels have been investigated by rotating bending fatigue tests. Results show that the fatigue limits (the fatigue strength at 107 cycles) were improved remarkably by plasma nitriding due to the high hardness of 1000Hv and compressive stress of 400MPa in the nitrided layer. Scanning electron microscopic observations show that after nitriding the fatigue crack initiation sites moved from the surface flaws or near-surface matrix into the AlN inclusions at around the case-core interface. Degassing treatment can increase the fatigue limit because it prevented fatigue crack initiation at AlN inclusions due to the reduced [N] contents and refined inclusion size.
Rotating bending fatigue properties of two case hardening steels after nitriding treatment
Zhou, Chao (Autor:in) / Wang, Maoqiu (Autor:in) / Hui, Weijun (Autor:in) / Dong, Han (Autor:in) / Wang, Lei (Autor:in) / Wu, Run (Autor:in)
24.08.2012
7 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Rotating bending fatigue properties of two case hardening steels after nitriding treatment
| British Library Online Contents | 2013
Fatigue properties of two case hardening steels after carburization
| British Library Online Contents | 2009
Influence of niobium microalloying on rotating bending fatigue properties of case carburized steels
| British Library Online Contents | 2008
Low-Cycle Fatigue of Steels After Ion Nitriding in Hydrogen-Free Atmospheres
| British Library Online Contents | 2016
Fatigue and hardening of steels
| Engineering Index Backfile | 1933