Processing map for hot working characteristics of a wrought 2205 duplex stainless steel
Abstract Processing map on a wrought 2205 duplex stainless steel under hot compression conditions has been developed based on the dynamic material model theories in the range 1223–1473K and 0.01–10s−1. The various domains in the map corresponding to different deformation characteristics have been discussed in combination of microstructural observations. The results show that the power dissipation efficiency (η) depends strongly on the dynamic recrystallization (DRX) of austenite which plays a dominant role in microstructural evolution, while the ferrite phase mainly continues to exhibit relatively well-developed dynamic recovery (DRV) at large strain. The optimum hot working domain of wrought 2205 duplex stainless steel is obtained to be in the temperature range 1373–1473K and at strain rate of 0.01s−1, with peak efficiency 50% occurring at about 1423K, in which more uniform microstructure is developed due to the occurrence of complete DRX of austenite. The unstable hot working regimes are predicted by Prasad instability criterion, in good agreement with the macro-and microstructural observations. As predicted, flow instability, which are manifested as twinning, bands of flow localization and the absence of DRX in austenite are observed at lower temperatures and higher strain rates (1223–1273K and 1–10s−1); in other cases, wedge cracking is responsible for instability phenomena observed at the temperature range 1373–1423K and strain rate of 10s−1.
Processing map for hot working characteristics of a wrought 2205 duplex stainless steel
Abstract Processing map on a wrought 2205 duplex stainless steel under hot compression conditions has been developed based on the dynamic material model theories in the range 1223–1473K and 0.01–10s−1. The various domains in the map corresponding to different deformation characteristics have been discussed in combination of microstructural observations. The results show that the power dissipation efficiency (η) depends strongly on the dynamic recrystallization (DRX) of austenite which plays a dominant role in microstructural evolution, while the ferrite phase mainly continues to exhibit relatively well-developed dynamic recovery (DRV) at large strain. The optimum hot working domain of wrought 2205 duplex stainless steel is obtained to be in the temperature range 1373–1473K and at strain rate of 0.01s−1, with peak efficiency 50% occurring at about 1423K, in which more uniform microstructure is developed due to the occurrence of complete DRX of austenite. The unstable hot working regimes are predicted by Prasad instability criterion, in good agreement with the macro-and microstructural observations. As predicted, flow instability, which are manifested as twinning, bands of flow localization and the absence of DRX in austenite are observed at lower temperatures and higher strain rates (1223–1273K and 1–10s−1); in other cases, wedge cracking is responsible for instability phenomena observed at the temperature range 1373–1423K and strain rate of 10s−1.
Processing map for hot working characteristics of a wrought 2205 duplex stainless steel
Chen, Lei (Autor:in) / Ma, Xiaocong (Autor:in) / Liu, Xiao (Autor:in) / Wang, Longmei (Autor:in)
24.09.2010
6 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Processing map for hot working characteristics of a wrought 2205 duplex stainless steel
British Library Online Contents | 2011
|Factors Affecting Corrosion of 2205 Duplex Stainless Steel
British Library Online Contents | 2014
|Hydrogen-enhanced cracking of 2205 duplex stainless steel
British Library Online Contents | 2007
|Hydrogen Embrittlement of SAF 2205 Duplex Stainless Steel
British Library Online Contents | 2002
|Sigma phase precipitation in duplex stainless steel 2205
British Library Online Contents | 2007
|