FLUORAPATITE-FORMING CALCIUM PHOSPHATE CEMENTS
This study reports in vitro and in vivo properties of fluorapatite (FA)-forming calcium phosphate cements (CPCs). Experimental cements contained from (0 to 3.1) mass % of F, corresponding to presence of FA at levels of approximately (0 to 87) mass %. The crystallinity of the apatitic cement product increased greatly with the FA content. When implanted subcutaneously in rats, the in vivo resorption rate decreased significantly with increasing FA content. The cement with the highest FA content was not resorbed in soft tissue, making it biocompatible and bioinert CPC. These bioinert CPCs are candidates for use in useful applications where slow or no resorption of the implant is required to achieve the desired clinical outcome.
L'invention porte sur des ciments au phosphate de calcium (CPC) formant de la fluorapatite (FA), dont les propriétés ont été étudiées in vitro et in vivo. Les ciments expérimentaux contenaient de 0 à 3,1 pour cent massique de F, ce qui correspond à une présence de fluorapatite à des niveaux compris entre 0 et 87 pour cent massique environ. La cristallinité du produit ciment apatitique augmentait considérablement en fonction de la teneur en fluorapatite. Lors de l'implantation sous-cutanée de ces ciments chez des rats, le taux de résorption in vivo diminuait de manière significative à mesure qu'augmentait la teneur en fluorapatite. Le ciment possédant la plus haute teneur en FA n'était pas résorbé par les tissus mous, ce qui en fait un CPC biocompatible et bio-inerte. Les CPC bio-inertes selon l'invention sont de bons candidats pour des applications utiles où l'implant doit présenter une résorption lente ou nulle afin d'atteindre le résultat clinique désiré.
FLUORAPATITE-FORMING CALCIUM PHOSPHATE CEMENTS
This study reports in vitro and in vivo properties of fluorapatite (FA)-forming calcium phosphate cements (CPCs). Experimental cements contained from (0 to 3.1) mass % of F, corresponding to presence of FA at levels of approximately (0 to 87) mass %. The crystallinity of the apatitic cement product increased greatly with the FA content. When implanted subcutaneously in rats, the in vivo resorption rate decreased significantly with increasing FA content. The cement with the highest FA content was not resorbed in soft tissue, making it biocompatible and bioinert CPC. These bioinert CPCs are candidates for use in useful applications where slow or no resorption of the implant is required to achieve the desired clinical outcome.
L'invention porte sur des ciments au phosphate de calcium (CPC) formant de la fluorapatite (FA), dont les propriétés ont été étudiées in vitro et in vivo. Les ciments expérimentaux contenaient de 0 à 3,1 pour cent massique de F, ce qui correspond à une présence de fluorapatite à des niveaux compris entre 0 et 87 pour cent massique environ. La cristallinité du produit ciment apatitique augmentait considérablement en fonction de la teneur en fluorapatite. Lors de l'implantation sous-cutanée de ces ciments chez des rats, le taux de résorption in vivo diminuait de manière significative à mesure qu'augmentait la teneur en fluorapatite. Le ciment possédant la plus haute teneur en FA n'était pas résorbé par les tissus mous, ce qui en fait un CPC biocompatible et bio-inerte. Les CPC bio-inertes selon l'invention sont de bons candidats pour des applications utiles où l'implant doit présenter une résorption lente ou nulle afin d'atteindre le résultat clinique désiré.
FLUORAPATITE-FORMING CALCIUM PHOSPHATE CEMENTS
CIMENTS AU PHOSPHATE DE CALCIUM FORMANT DE LA FLUORAPATITE
CHOW LAURENCE C (Autor:in) / TAKAGI SHOZO (Autor:in)
06.11.2018
Patent
Elektronische Ressource
Englisch
IPC:
A61L
Verfahren oder Vorrichtungen zum Sterilisieren von Stoffen oder Gegenständen allgemein
,
METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL
/
A61K
Zubereitungen für medizinische, zahnärztliche oder kosmetische Zwecke
,
PREPARATIONS FOR MEDICAL, DENTAL, OR TOILET PURPOSES
/
C04B
Kalk
,
LIME
Sodium Phosphate-Derived Calcium Phosphate Cements
| British Library Online Contents | 1995
Sodium phosphate-derived calcium phosphate cements
| Tema Archiv | 1995
Sodium Phosphate-Derived Calcium Phosphate Cements
| Online Contents | 1995
Potassium Containing Apatitic Calcium Phosphate Cements
| British Library Online Contents | 2004