Preparation method for clinker of cement raw material burnability test
The invention belongs to the field of the cement production test, specifically relates to a preparation method for a clinker of a cement raw material burnability test. The preparation method comprises the following steps: a, according to the weight volume ratio cement raw material : distilled water = 5 g : 1 mL, uniformly mixing the both to obtain the wet raw material; b, weighing the wet raw material and placing in a circular forming mould to press and prepare a cake test body; and c, drying the cake test body for 2-3 h in 95-115 DEG C, burning from 400 DEG C to 950 DEG C for 30 min in the speed of 19-21 DEG C/min after taking, and burning for 30 min from the current temperature to the test temperature in the speed of 9-11 DEG C/min, then taking out and cooling at the ventilation position for future use. The method is convenient, fast, and safe, and is the better method for preparing the clinker of the cement raw material burnability test.
Preparation method for clinker of cement raw material burnability test
The invention belongs to the field of the cement production test, specifically relates to a preparation method for a clinker of a cement raw material burnability test. The preparation method comprises the following steps: a, according to the weight volume ratio cement raw material : distilled water = 5 g : 1 mL, uniformly mixing the both to obtain the wet raw material; b, weighing the wet raw material and placing in a circular forming mould to press and prepare a cake test body; and c, drying the cake test body for 2-3 h in 95-115 DEG C, burning from 400 DEG C to 950 DEG C for 30 min in the speed of 19-21 DEG C/min after taking, and burning for 30 min from the current temperature to the test temperature in the speed of 9-11 DEG C/min, then taking out and cooling at the ventilation position for future use. The method is convenient, fast, and safe, and is the better method for preparing the clinker of the cement raw material burnability test.
Preparation method for clinker of cement raw material burnability test
DENG LEI (Autor:in) / TONG MENGJUAN (Autor:in) / QI TAOJUN (Autor:in)
08.04.2015
Patent
Elektronische Ressource
Englisch
IPC:
C04B
Kalk
,
LIME
High chlorine cement clinker with improved burnability
| Europäisches Patentamt | 2022
Coating and Burnability of Clinker
| Springer Verlag | 2019
Burnability Studies with Mineralizers/Fluxes in Clinker Manufacture
| British Library Conference Proceedings | 1994