Preparation method of transparent tetravalent chromium-doped yttrium aluminum garnet ceramics
The invention relates to a preparation method of transparent tetravalent chromium-doped yttrium aluminum garnet ceramics. The preparation method comprises the following steps: weighing raw material powder according to a stoichiometric ratio of a to-be-prepared ceramic component structural formula (Al1-xCrx)5CayY3-yO12 (x is not smaller than 0.001 and not larger than 0.01, and y is not smaller than 10x and not larger than 40x); adding a sintering aid and a charge compensating agent; mixing by ball-milling to obtain a slurry material; drying and sieving the slurry material and then molding to obtain a biscuit; calcining to remove volatile impurities; sintering the biscuit in vacuum at the temperature of 1730 to 1850 DEG C for 4 to 30 hours; subsequently annealing in air at the temperature of 1300 to 1550 DEG C for 10 to 25 hours to obtain compact Cr<4+>:YAG transparent ceramics. The Cr<4+>:YAG transparent ceramics prepared by the method disclosed by the invention are high in compactness, good in uniformity, free of segregation, reasonable in grain graduation distribution, free of abnormal grain growth, free of grain interior and intergranular pores and high in penetration rate, and have the conditions for being a laser gain medium.
Preparation method of transparent tetravalent chromium-doped yttrium aluminum garnet ceramics
The invention relates to a preparation method of transparent tetravalent chromium-doped yttrium aluminum garnet ceramics. The preparation method comprises the following steps: weighing raw material powder according to a stoichiometric ratio of a to-be-prepared ceramic component structural formula (Al1-xCrx)5CayY3-yO12 (x is not smaller than 0.001 and not larger than 0.01, and y is not smaller than 10x and not larger than 40x); adding a sintering aid and a charge compensating agent; mixing by ball-milling to obtain a slurry material; drying and sieving the slurry material and then molding to obtain a biscuit; calcining to remove volatile impurities; sintering the biscuit in vacuum at the temperature of 1730 to 1850 DEG C for 4 to 30 hours; subsequently annealing in air at the temperature of 1300 to 1550 DEG C for 10 to 25 hours to obtain compact Cr<4+>:YAG transparent ceramics. The Cr<4+>:YAG transparent ceramics prepared by the method disclosed by the invention are high in compactness, good in uniformity, free of segregation, reasonable in grain graduation distribution, free of abnormal grain growth, free of grain interior and intergranular pores and high in penetration rate, and have the conditions for being a laser gain medium.
Preparation method of transparent tetravalent chromium-doped yttrium aluminum garnet ceramics
ZHANG LE (Autor:in) / ZHOU TIANYUAN (Autor:in) / WANG CHENG (Autor:in)
29.04.2015
Patent
Elektronische Ressource
Englisch
IPC:
C04B
Kalk
,
LIME
METHOD OF OBTAINING TRANSPARENT CERAMICS OF YTTRIUM-ALUMINUM GARNET
| Europäisches Patentamt | 2019
Samarium Ions Doped Yttrium Aluminum Garnet Glass Ceramics
| British Library Online Contents | 2013
| British Library Online Contents | 2007
| British Library Online Contents | 2004
Preparation method of thulium-holmium double-doped yttrium aluminum garnet laser transparent ceramic
| Europäisches Patentamt | 2021