Ultralow-dielectric-constant microwave dielectric ceramic EuYV2O8 having near-zero resonance frequency temperature coefficient
The invention discloses ultralow-dielectric-constant microwave dielectric ceramic EuYV2O8 having a near-zero resonance frequency temperature coefficient and adopting a tetragonal zirconia structure as well as a preparation method of the microwave dielectric ceramic EuYV2O8. The method comprises steps as follows: (1) original Eu2O3, Y2O3 and V2O5 powder with the purity higher than 99.9% (weight percentage) is weighed and prepared according to composition of the EuYV2O8; (2) the raw material in Step (1) is subjected to wet ball milling and mixing for 12 h, distilled water serves as a ball milling medium, and pre-sintering is performed in the atmosphere at the temperature of 800 DEG C for 6 h after drying; (3) a binder is added to powder obtained in Step (2), granulation and compression molding are performed, and finally, sintering is performed in the atmosphere at the temperature of 850-900 DEG C for 4 h, wherein a polyvinyl alcohol solution with the mass concentration of 5% serves as the binder and the adding amount of polyvinyl alcohol accounts for 3% of the total mass of the powder. The prepared ceramic is well sintered at the temperature lower than 900 DEG C, the dielectric constant is 11.7-12.4, the Qf (quality factor) value is up to 125000-173000 GHz, the resonance frequency temperature coefficient is low, and the ceramic has the great industrial application value.
Ultralow-dielectric-constant microwave dielectric ceramic EuYV2O8 having near-zero resonance frequency temperature coefficient
The invention discloses ultralow-dielectric-constant microwave dielectric ceramic EuYV2O8 having a near-zero resonance frequency temperature coefficient and adopting a tetragonal zirconia structure as well as a preparation method of the microwave dielectric ceramic EuYV2O8. The method comprises steps as follows: (1) original Eu2O3, Y2O3 and V2O5 powder with the purity higher than 99.9% (weight percentage) is weighed and prepared according to composition of the EuYV2O8; (2) the raw material in Step (1) is subjected to wet ball milling and mixing for 12 h, distilled water serves as a ball milling medium, and pre-sintering is performed in the atmosphere at the temperature of 800 DEG C for 6 h after drying; (3) a binder is added to powder obtained in Step (2), granulation and compression molding are performed, and finally, sintering is performed in the atmosphere at the temperature of 850-900 DEG C for 4 h, wherein a polyvinyl alcohol solution with the mass concentration of 5% serves as the binder and the adding amount of polyvinyl alcohol accounts for 3% of the total mass of the powder. The prepared ceramic is well sintered at the temperature lower than 900 DEG C, the dielectric constant is 11.7-12.4, the Qf (quality factor) value is up to 125000-173000 GHz, the resonance frequency temperature coefficient is low, and the ceramic has the great industrial application value.
Ultralow-dielectric-constant microwave dielectric ceramic EuYV2O8 having near-zero resonance frequency temperature coefficient
TANG YING (Autor:in) / FANG LIANG (Autor:in) / FANG WEISHUANG (Autor:in)
25.11.2015
Patent
Elektronische Ressource
Englisch
IPC:
C04B
Kalk
,
LIME
| Europäisches Patentamt | 2015
| Europäisches Patentamt | 2015
Temperature stable ultralow dielectric constant microwave dielectric ceramic LiZnYbV2O8
| Europäisches Patentamt | 2016
Temperature-stable ultralow-dielectric-constant microwave dielectric ceramic LiMgV5O14
| Europäisches Patentamt | 2015
Stable-temperature ultralow-dielectric-constant microwave dielectric ceramic SrLi3Eu3Mo2O13
| Europäisches Patentamt | 2015