Glass waste residue ceramic water permeable brick and preparation process thereof
The invention discloses a glass waste residue ceramic water permeable brick which comprises a backing material and a surface material, wherein the backing material is prepared from the following components in parts by weight: ceramic waste added to make the total amount be 100 parts, 5-8 parts of a binder, 2-4 parts of water and 5-20 parts of glass waste residues; the ceramic waste material is composed of 5-15 parts of ceramic waste with the particle size of 30 mesh or above and the balance being ceramic waste with the particle size of 30 mesh or below; the particle size of the glass waste residues is 40-200 mesh. The surface material is prepared from the following components in parts by weight: ceramic waste added to make the total amount be 100 parts, 4-10 parts of a binder and 2-4 partsof water. The glass waste residue ceramic water permeable brick has high strength and water permeability coefficient, the firing temperature of the brick is lower than that of a common water permeable brick, the brick is more energy-saving, low-carbon and environment-friendly, and the quality index of the obtained water permeable brick meets the national standard.
本发明公开了一种玻璃废渣陶瓷透水砖，包括底料和面料；其中，底料由按重量份的以下组分制成：补足100份的陶瓷废料、5‑8份的粘结剂、2‑4份的水和5‑20份的玻璃废渣；其中，陶瓷废料由5‑15份30目以上陶瓷废料和余量的30目以下的陶瓷废料组成；所述玻璃废渣的粒径为40‑200目；所述面料由按重量份计的以下组分制成：补足100份的陶瓷废料、4‑10份粘结剂和2‑4份水。该玻璃废渣陶瓷透水砖具有较高的强度和透水系数，其烧成温度相对于普通的透水砖低，更加节能低碳环保，得到的透水砖的质量指标符合国家标准。
Glass waste residue ceramic water permeable brick and preparation process thereof
The invention discloses a glass waste residue ceramic water permeable brick which comprises a backing material and a surface material, wherein the backing material is prepared from the following components in parts by weight: ceramic waste added to make the total amount be 100 parts, 5-8 parts of a binder, 2-4 parts of water and 5-20 parts of glass waste residues; the ceramic waste material is composed of 5-15 parts of ceramic waste with the particle size of 30 mesh or above and the balance being ceramic waste with the particle size of 30 mesh or below; the particle size of the glass waste residues is 40-200 mesh. The surface material is prepared from the following components in parts by weight: ceramic waste added to make the total amount be 100 parts, 4-10 parts of a binder and 2-4 partsof water. The glass waste residue ceramic water permeable brick has high strength and water permeability coefficient, the firing temperature of the brick is lower than that of a common water permeable brick, the brick is more energy-saving, low-carbon and environment-friendly, and the quality index of the obtained water permeable brick meets the national standard.
本发明公开了一种玻璃废渣陶瓷透水砖，包括底料和面料；其中，底料由按重量份的以下组分制成：补足100份的陶瓷废料、5‑8份的粘结剂、2‑4份的水和5‑20份的玻璃废渣；其中，陶瓷废料由5‑15份30目以上陶瓷废料和余量的30目以下的陶瓷废料组成；所述玻璃废渣的粒径为40‑200目；所述面料由按重量份计的以下组分制成：补足100份的陶瓷废料、4‑10份粘结剂和2‑4份水。该玻璃废渣陶瓷透水砖具有较高的强度和透水系数，其烧成温度相对于普通的透水砖低，更加节能低碳环保，得到的透水砖的质量指标符合国家标准。
Glass waste residue ceramic water permeable brick and preparation process thereof
一种玻璃废渣陶瓷透水砖及其制备工艺
ZHOU WEIJUN (Autor:in) / FAN GUOXIONG (Autor:in) / HU QICHENG (Autor:in) / CAI SHIJIE (Autor:in) / ZENG RUI (Autor:in)
10.04.2020
Patent
Elektronische Ressource
Chinesisch
Aluminum ore waste residue ceramic water permeable brick and preparation process thereof
| Europäisches Patentamt | 2020
Nickel ore waste residue ceramic water permeable brick and preparation process thereof
| Europäisches Patentamt | 2020
Phosphogypsum ceramic water permeable brick and preparation method thereof
| Europäisches Patentamt | 2023
Water permeable brick and preparation process thereof
| Europäisches Patentamt | 2021
Method for manufacturing water permeable brick by combining waste glass with waste ceramic
| Europäisches Patentamt | 2020