Ceramic part component material capable of being quickly fired and preparation method
The invention discloses a ceramic part component material capable of being quickly fired and a preparation method. The ceramic part component material is prepared from 9350 parts of aluminum oxide, 35parts of light calcium carbonate, 100 parts of quartz powder, 100 parts of Suzhou 1# earth, 92 parts of light magnesium oxide, 4 parts of chromium oxide, 65 parts of lanthanum oxide, 400 parts of aluminum nitride and 1150 parts of paraffin. The quantity of the oleic acid is calculated according to the proportion that 93.5 kg of aluminum oxide corresponds to 950 ml. The materials are selected according to an excellent proportion, and the production is carried out according to requirements in combination with a production and preparation method, so that a fired ceramic part faster than a traditional fired ceramic part can be obtained.
本发明公开了一种可快速烧制的陶瓷件组份料及制备方法，氧化铝9350份，轻质碳酸钙35份，石英粉100份，苏州1#土100份，轻质氧化镁92份，氧化铬4份，氧化镧65份，氮化铝400份，石蜡1150份；油酸量按照氧化铝93.5千克为950毫升同比例计算，通过精良的配比选料用料，并结合生产制备方法按照要求进行生产，能够得到相比传统烧制更快的烧制陶瓷件。
Ceramic part component material capable of being quickly fired and preparation method
The invention discloses a ceramic part component material capable of being quickly fired and a preparation method. The ceramic part component material is prepared from 9350 parts of aluminum oxide, 35parts of light calcium carbonate, 100 parts of quartz powder, 100 parts of Suzhou 1# earth, 92 parts of light magnesium oxide, 4 parts of chromium oxide, 65 parts of lanthanum oxide, 400 parts of aluminum nitride and 1150 parts of paraffin. The quantity of the oleic acid is calculated according to the proportion that 93.5 kg of aluminum oxide corresponds to 950 ml. The materials are selected according to an excellent proportion, and the production is carried out according to requirements in combination with a production and preparation method, so that a fired ceramic part faster than a traditional fired ceramic part can be obtained.
本发明公开了一种可快速烧制的陶瓷件组份料及制备方法，氧化铝9350份，轻质碳酸钙35份，石英粉100份，苏州1#土100份，轻质氧化镁92份，氧化铬4份，氧化镧65份，氮化铝400份，石蜡1150份；油酸量按照氧化铝93.5千克为950毫升同比例计算，通过精良的配比选料用料，并结合生产制备方法按照要求进行生产，能够得到相比传统烧制更快的烧制陶瓷件。
Ceramic part component material capable of being quickly fired and preparation method
一种可快速烧制的陶瓷件组份料及制备方法
XI WEIPING (Autor:in) / MEI QINFANG (Autor:in) / SUN HAIQIANG (Autor:in) / ZHU QIANG (Autor:in) / WANG LIANXIA (Autor:in) / YANG QIN (Autor:in)
01.05.2020
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
ZIRCONIA MOLDED ARTICLE CAPABLE OF BEING FIRED QUICKLY AND CALCINATED BODY
| Europäisches Patentamt | 2022
ZIRCONIA MOLDED ARTICLE CAPABLE OF BEING FIRED QUICKLY AND CALCINATED BODY
| Europäisches Patentamt | 2020
Cement handicraft material capable of being quickly demolded and preparation method thereof
| Europäisches Patentamt | 2021
Concrete structure metal component capable of being quickly disassembled
| Europäisches Patentamt | 2024
Ceramic adhesive capable of being fired and application thereof
| Europäisches Patentamt | 2024