    Method for producing a pyrolytic carbon with predetermined microstructure

    Neue Suche nach: DELEHOUZE ARNAUD
    Neue Suche nach: LORRIAUX AMANDINE
    Neue Suche nach: MAILLE LAURENCE
    Neue Suche nach: DAVID PATRICK

    The invention concerns a method for producing pyrolytic carbon, comprising a step of forming the pyrolytic carbon by a Leidenfrost effect from at least one C2 to C6 polyalcohol or alcohol precursor, the precursor being ethanol or a C3 polyalcohol or alcohol, and, when ethanol is used as precursor, the rough laminar pyrolytic carbon being obtained by imposing a temperature of between 1250 DEG C and1325 DEG C during the Leidenfrost effect.

    本发明涉及一种制造热解碳的方法，其包括由至少一种C至C多元醇或醇前驱体通过莱登弗罗斯特效应形成热解碳的步骤，前驱体为乙醇或C多元醇或醇，并且当使用乙醇作为前驱体时，通过在莱登弗罗斯特效应期间施加1250℃至1325℃之间的温度而获得粗糙的层状热解碳。

    Zugriff

    Download

    Zugriff

    Download

    Seitennavigation

    Dokumentinformationen
    Ähnliche Titel

    Exportieren, teilen und zitieren

    Method for producing a pyrolytic carbon with predetermined microstructure

    Neue Suche nach: DELEHOUZE ARNAUD
    Neue Suche nach: LORRIAUX AMANDINE
    Neue Suche nach: MAILLE LAURENCE
    Neue Suche nach: DAVID PATRICK

    The invention concerns a method for producing pyrolytic carbon, comprising a step of forming the pyrolytic carbon by a Leidenfrost effect from at least one C2 to C6 polyalcohol or alcohol precursor, the precursor being ethanol or a C3 polyalcohol or alcohol, and, when ethanol is used as precursor, the rough laminar pyrolytic carbon being obtained by imposing a temperature of between 1250 DEG C and1325 DEG C during the Leidenfrost effect.

    本发明涉及一种制造热解碳的方法，其包括由至少一种C至C多元醇或醇前驱体通过莱登弗罗斯特效应形成热解碳的步骤，前驱体为乙醇或C多元醇或醇，并且当使用乙醇作为前驱体时，通过在莱登弗罗斯特效应期间施加1250℃至1325℃之间的温度而获得粗糙的层状热解碳。

    Zugriff

    Download

    Method for producing a pyrolytic carbon with predetermined microstructure

    Neue Suche nach: DELEHOUZE ARNAUD
    Neue Suche nach: LORRIAUX AMANDINE
    Neue Suche nach: MAILLE LAURENCE
    Neue Suche nach: DAVID PATRICK

    The invention concerns a method for producing pyrolytic carbon, comprising a step of forming the pyrolytic carbon by a Leidenfrost effect from at least one C2 to C6 polyalcohol or alcohol precursor, the precursor being ethanol or a C3 polyalcohol or alcohol, and, when ethanol is used as precursor, the rough laminar pyrolytic carbon being obtained by imposing a temperature of between 1250 DEG C and1325 DEG C during the Leidenfrost effect.

    本发明涉及一种制造热解碳的方法，其包括由至少一种C至C多元醇或醇前驱体通过莱登弗罗斯特效应形成热解碳的步骤，前驱体为乙醇或C多元醇或醇，并且当使用乙醇作为前驱体时，通过在莱登弗罗斯特效应期间施加1250℃至1325℃之间的温度而获得粗糙的层状热解碳。

    Zugriff

    Download

    Zugriff

    Download

    Seitennavigation

    Dokumentinformationen
    Ähnliche Titel

    Exportieren, teilen und zitieren

    Dokumentinformationen
    Titel:

    Method for producing a pyrolytic carbon with predetermined microstructure

    Weitere Titelangaben:

    制造具有预定微结构的热解碳的方法

    Beteiligte:

    DELEHOUZE ARNAUD (Autor:in) / LORRIAUX AMANDINE (Autor:in) / MAILLE LAURENCE (Autor:in) / DAVID PATRICK (Autor:in)

    Erscheinungsdatum:

    29.05.2020

    Medientyp:

    Patent

    Format:

    Elektronische Ressource

    Sprache:

    Chinesisch

    Klassifikation:

    IPC:  C04B Kalk , LIME / C01B NON-METALLIC ELEMENTS , Nichtmetallische Elemente

    Ähnliche Titel

    Method for producing a pyrolytic carbon with predetermined microstructure

    DELEHOUZE ARNAUD / LORRIAUX AMANDINE / MAILLE LAURENCE et al. | Europäisches Patentamt | 2022

    Freier Zugriff

    METHOD FOR PRODUCING A PYROLYTIC CARBON WITH PREDETERMINED MICROSTRUCTURE

    DELEHOUZE ARNAUD / LORRIAUX AMANDINE / MAILLE LAURENCE et al. | Europäisches Patentamt | 2021

    Freier Zugriff

    Microstructure of Pyrolytic Carbon Matrix in Carbon/Carbon Composites after Graphitization

    Sun, W. C. / Li, H. J. / Zhang, S. Y. et al. | British Library Online Contents | 2007

    Flexural strength predetermined

    Bauman, E.W. | Engineering Index Backfile | 1935

    Tribological properties of carbon/carbon composites with various pyrolytic carbon microstructures

    Yu, S. / Zhang, F. / Xiong, X. et al. | British Library Online Contents | 2013

    Nach oben