FIRE-RESISTANT SULFUR CONCRETE
A sulfur concrete has constituents that include a coarse aggregate in an amount in a range of 40-50 wt% of the weight of the sulfur concrete, a fine aggregate in an amount in a range of 20-40 wt% of the weight of the sulfur concrete, a fine filler in an amount in a range of 8-12 wt% of the weight of the sulfur concrete, and a binder in an amount in a range of 12- 20 wt% of the weight of the sulfurconcrete. The binder includes elemental sulfur in an amount in a range of 25-60 wt % of the weight of the binder and asphalt in an amount in a range of 40-75 wt % of the weight of the binder.
硫磺混凝土的成分包含：含量在硫磺混凝土重量的40重量％至50重量％范围内的粗骨料、含量在硫磺混凝土重量的20重量％至40重量％范围内的细骨料、含量在硫磺混凝土重量的8重量％至12重量％范围内的细填料以及含量在硫磺混凝土重量的12重量％至20重量％范围内的粘结剂。粘结剂包含：含量在粘结剂重量的25重量％至60重量％范围内的元素硫以及含量在粘结剂重量的40重量％至75重量％范围内的沥青。
FIRE-RESISTANT SULFUR CONCRETE
A sulfur concrete has constituents that include a coarse aggregate in an amount in a range of 40-50 wt% of the weight of the sulfur concrete, a fine aggregate in an amount in a range of 20-40 wt% of the weight of the sulfur concrete, a fine filler in an amount in a range of 8-12 wt% of the weight of the sulfur concrete, and a binder in an amount in a range of 12- 20 wt% of the weight of the sulfurconcrete. The binder includes elemental sulfur in an amount in a range of 25-60 wt % of the weight of the binder and asphalt in an amount in a range of 40-75 wt % of the weight of the binder.
硫磺混凝土的成分包含：含量在硫磺混凝土重量的40重量％至50重量％范围内的粗骨料、含量在硫磺混凝土重量的20重量％至40重量％范围内的细骨料、含量在硫磺混凝土重量的8重量％至12重量％范围内的细填料以及含量在硫磺混凝土重量的12重量％至20重量％范围内的粘结剂。粘结剂包含：含量在粘结剂重量的25重量％至60重量％范围内的元素硫以及含量在粘结剂重量的40重量％至75重量％范围内的沥青。
FIRE-RESISTANT SULFUR CONCRETE
耐火硫磺混凝土
AL-IDI SALEH H (Autor:in) / AL-MEHTHEL MOHAMMED H (Autor:in) / ALI MOHAMMED RIZWAN (Autor:in) / MASLEHUDDIN MOHAMMED (Autor:in)
10.07.2020
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
/
C08K
Verwendung von anorganischen oder nichtmakromolekularen organischen Stoffen als Zusatzstoffe
,
USE OF INORGANIC OR NON-MACROMOLECULAR ORGANIC SUBSTANCES AS COMPOUNDING INGREDIENTS
/
C08L
COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
,
Massen auf Basis makromolekularer Verbindungen
British Library Online Contents | 2000