Medium-temperature bright red glaze and preparation method thereof
The invention discloses a medium-temperature bright red glaze and a preparation method thereof. The medium-temperature bright red glaze is prepared from the following raw materials in percentage by weight: 22-28% of potassium feldspar, 3-6% of albite, 10-15% of frit, 4-8% of Sanbao powder, 12-19% of quartz powder, 10-15% of calcite, 0.8-3% of zinc oxide, 1-4% of zirconium silicate, 8-12% of kaolin, 1-3% of talcum powder and 0.7-2% of wollastonite. The glaze has the beneficial effects that the glaze is smooth in hand feeling, uniform in color, durable, resistant to abrasion, good in smoothnessand thermal stability and wide in firing range, the range brightness is good when the temperature ranges from 1,195 DEG C to 1,250 DEG C, color development is bright, the standard of high-quality porcelain is met, and the glaze is suitable for being widely popularized.
本发明公开了一种中温大红色釉料及其制备方法，由以下配比的原料组成：钾长石22‑28％，钠长石3‑6％，熔块10‑15％，三宝粉4‑8％，石英粉12‑19％，方解石10‑15％，氧化锌0.8‑3％，硅酸锆1‑4％，高岭土8‑12％，滑石粉1‑3％，硅灰石0.7‑2％。有益效果在于：本发明的釉料手感平滑、颜色均匀，经久、耐磨、光洁度与热稳定性好，烧成范围广，达到1195‑1250℃之间时范围亮度佳，发色鲜艳，符合优质瓷器的标准，适合广泛推广。
Medium-temperature bright red glaze and preparation method thereof
The invention discloses a medium-temperature bright red glaze and a preparation method thereof. The medium-temperature bright red glaze is prepared from the following raw materials in percentage by weight: 22-28% of potassium feldspar, 3-6% of albite, 10-15% of frit, 4-8% of Sanbao powder, 12-19% of quartz powder, 10-15% of calcite, 0.8-3% of zinc oxide, 1-4% of zirconium silicate, 8-12% of kaolin, 1-3% of talcum powder and 0.7-2% of wollastonite. The glaze has the beneficial effects that the glaze is smooth in hand feeling, uniform in color, durable, resistant to abrasion, good in smoothnessand thermal stability and wide in firing range, the range brightness is good when the temperature ranges from 1,195 DEG C to 1,250 DEG C, color development is bright, the standard of high-quality porcelain is met, and the glaze is suitable for being widely popularized.
本发明公开了一种中温大红色釉料及其制备方法，由以下配比的原料组成：钾长石22‑28％，钠长石3‑6％，熔块10‑15％，三宝粉4‑8％，石英粉12‑19％，方解石10‑15％，氧化锌0.8‑3％，硅酸锆1‑4％，高岭土8‑12％，滑石粉1‑3％，硅灰石0.7‑2％。有益效果在于：本发明的釉料手感平滑、颜色均匀，经久、耐磨、光洁度与热稳定性好，烧成范围广，达到1195‑1250℃之间时范围亮度佳，发色鲜艳，符合优质瓷器的标准，适合广泛推广。
Medium-temperature bright red glaze and preparation method thereof
一种中温大红色釉料及其制备方法
HUANG WEIYOU (Autor:in)
14.07.2020
Patent
Elektronische Ressource
Chinesisch
Bright red glaze rock plate and preparation method thereof
| Europäisches Patentamt | 2021
Bright glaze for ceramic archaized brick, and preparation method thereof
| Europäisches Patentamt | 2020
Bright green double-layer transmutation glaze and preparation method thereof
| Europäisches Patentamt | 2023
| Europäisches Patentamt | 2023
Glaze used for medium-temperature ceramic product and ceramic preparation method applying glaze
| Europäisches Patentamt | 2015