Cordierite microwave dielectric ceramic material and preparation method thereof
The invention discloses a cordierite microwave dielectric ceramic material and a preparation method thereof, and belongs to the technical field of electronic ceramic materials. The ceramic material comprises the components in percentage by mass: 13 to 18 wt% of MgO, 28 to 37 wt% of Al2O3, 45 to 55 wt% of SiO2, 0 to 10 wt% of TiO2 and 0 to 5 wt% of ZrO2. The method is simple in process and low in raw material cost; the obtained microwave dielectric ceramic material has excellent properties of low dielectric constant and high quality factor, the dielectric constant is 4-6, the quality factor Q*fvalue is 60000-90000 GHz, the loss is reduced, and the signal transmission speed is increased; and the frequency temperature coefficient is less than +/-15 ppm/DEG C, so that the temperature stability is improved.
一种堇青石微波介质陶瓷材料及其制备方法,属于电子陶瓷材料技术领域。所述陶瓷材料各组分的质量百分比为:MgO为13~18wt%,AlO为28~37wt%,SiO为45~55wt%,TiO为0~10wt%,ZrO为0~5wt%。本发明工艺简单,原材料成本低;得到的微波介质陶瓷材料兼具低介电常数、高品质因数的优异性能,介电常数为4~6,品质因数Q×f值为60000~90000GHz,降低了损耗,提高了信号传输速度;频率温度系数小于±15ppm/℃,提高了温度稳定性。
Cordierite microwave dielectric ceramic material and preparation method thereof
The invention discloses a cordierite microwave dielectric ceramic material and a preparation method thereof, and belongs to the technical field of electronic ceramic materials. The ceramic material comprises the components in percentage by mass: 13 to 18 wt% of MgO, 28 to 37 wt% of Al2O3, 45 to 55 wt% of SiO2, 0 to 10 wt% of TiO2 and 0 to 5 wt% of ZrO2. The method is simple in process and low in raw material cost; the obtained microwave dielectric ceramic material has excellent properties of low dielectric constant and high quality factor, the dielectric constant is 4-6, the quality factor Q*fvalue is 60000-90000 GHz, the loss is reduced, and the signal transmission speed is increased; and the frequency temperature coefficient is less than +/-15 ppm/DEG C, so that the temperature stability is improved.
一种堇青石微波介质陶瓷材料及其制备方法,属于电子陶瓷材料技术领域。所述陶瓷材料各组分的质量百分比为:MgO为13~18wt%,AlO为28~37wt%,SiO为45~55wt%,TiO为0~10wt%,ZrO为0~5wt%。本发明工艺简单,原材料成本低;得到的微波介质陶瓷材料兼具低介电常数、高品质因数的优异性能,介电常数为4~6,品质因数Q×f值为60000~90000GHz,降低了损耗,提高了信号传输速度;频率温度系数小于±15ppm/℃,提高了温度稳定性。
Cordierite microwave dielectric ceramic material and preparation method thereof
一种堇青石微波介质陶瓷材料及其制备方法
ZHOU XIAOHUA (Autor:in) / PENG CHANG (Autor:in) / TANG BIN (Autor:in)
17.07.2020
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
Nonmetal mineral cordierite type microwave dielectric ceramic and preparation method thereof
Europäisches Patentamt | 2024
|Europäisches Patentamt | 2021
|Europäisches Patentamt | 2020
|Rare earth doped cordierite ceramic material and preparation method thereof
Europäisches Patentamt | 2023
|Cordierite porous ceramic and preparation method thereof
Europäisches Patentamt | 2023
|