High-cohesiveness moisture-resistant ceramic tile adhesive and preparation method thereof
The invention belongs to the technical field of binder production and preparation. The invention relates to a high-cohesiveness moisture-resistant ceramic tile adhesive and a preparation method thereof. The ceramic tile adhesive is prepared from the following raw materials in parts by weight: 30-40 parts of cement, 35-40 parts of river sand, 15-20 parts of polishing waste residues, 10-15 parts ofdispersible latex powder, 20-30 parts of starch, 0.2-0.5 part of borax, 0.1-0.3 part of caustic soda, 5-8 parts of heavy calcium carbonate, 5-8 parts of ash calcium, 0.2-0.6 part of hydroxypropyl methyl cellulose, 0.2-0.5 part of a bactericide and 0.1-0.3 part of a preservative. The ceramic tile adhesive is prepared by the preparation method, the ceramic tile adhesive has the advantages of no toxicity, environmental protection, excellent moisture resistance, excellent water resistance, high bonding strength, great improvement of the tensile adhesive strength of the ceramic tile adhesive afterimmersion in water and thermal aging, effective avoiding of the quality problems of shrinkage cracks, mildew, hollowing and even shedding of ceramic tiles, simple preparation process, and high economic values.
本发明属于粘结剂生产制备技术领域，尤其为一种粘结性强抗潮的瓷砖粘结剂及其制备方法，所述瓷砖粘结剂是由下列重量份的原料制成：水泥30～40份、河沙35～40份、抛光废渣15～20份、可分散乳胶粉10～15份、淀粉20～30份、硼砂0.2～0.5份、苛性钠0.1～0.3份、重钙5～8份、灰钙5～8份、羟丙基甲基纤维素0.2～0.6份、杀菌剂0.2～0.5份、防腐剂0.1～0.3份。本发明制备方法制得的瓷砖粘结剂，具有无毒环保以及优良的耐潮、耐水性能，粘结强度高，极大地提高了瓷砖粘结剂浸水后及热老化后的拉伸胶粘强度，有效避免瓷砖产生收缩裂缝、霉变、空鼓甚至脱落等质量问题，且制备工艺简单，具有较高的经济价值。
High-cohesiveness moisture-resistant ceramic tile adhesive and preparation method thereof
The invention belongs to the technical field of binder production and preparation. The invention relates to a high-cohesiveness moisture-resistant ceramic tile adhesive and a preparation method thereof. The ceramic tile adhesive is prepared from the following raw materials in parts by weight: 30-40 parts of cement, 35-40 parts of river sand, 15-20 parts of polishing waste residues, 10-15 parts ofdispersible latex powder, 20-30 parts of starch, 0.2-0.5 part of borax, 0.1-0.3 part of caustic soda, 5-8 parts of heavy calcium carbonate, 5-8 parts of ash calcium, 0.2-0.6 part of hydroxypropyl methyl cellulose, 0.2-0.5 part of a bactericide and 0.1-0.3 part of a preservative. The ceramic tile adhesive is prepared by the preparation method, the ceramic tile adhesive has the advantages of no toxicity, environmental protection, excellent moisture resistance, excellent water resistance, high bonding strength, great improvement of the tensile adhesive strength of the ceramic tile adhesive afterimmersion in water and thermal aging, effective avoiding of the quality problems of shrinkage cracks, mildew, hollowing and even shedding of ceramic tiles, simple preparation process, and high economic values.
本发明属于粘结剂生产制备技术领域，尤其为一种粘结性强抗潮的瓷砖粘结剂及其制备方法，所述瓷砖粘结剂是由下列重量份的原料制成：水泥30～40份、河沙35～40份、抛光废渣15～20份、可分散乳胶粉10～15份、淀粉20～30份、硼砂0.2～0.5份、苛性钠0.1～0.3份、重钙5～8份、灰钙5～8份、羟丙基甲基纤维素0.2～0.6份、杀菌剂0.2～0.5份、防腐剂0.1～0.3份。本发明制备方法制得的瓷砖粘结剂，具有无毒环保以及优良的耐潮、耐水性能，粘结强度高，极大地提高了瓷砖粘结剂浸水后及热老化后的拉伸胶粘强度，有效避免瓷砖产生收缩裂缝、霉变、空鼓甚至脱落等质量问题，且制备工艺简单，具有较高的经济价值。
High-cohesiveness moisture-resistant ceramic tile adhesive and preparation method thereof
一种粘结性强抗潮的瓷砖粘结剂及其制备方法
ZHOU QIHUA (Autor:in)
14.08.2020
Patent