Iron red gold ring glaze and preparation process of iron red gold ring glaze ceramic
The invention relates to the field of glaze and ceramic preparation processes. The iron oxide red gold ring glaze is characterized in that a raw material formula of the glaze comprises the following components in parts by weight: 42-46 parts of feldspar, 8-10 parts of kaolin, 6-7 parts of limestone, 5-8 parts of talcum powder, 12-14 parts of quartz, 10-14 parts of bone ash, 13-17 parts of industrial iron oxide red powder and 7-9 parts of glaze loess. The iron red gold ring glaze and the preparation process of the iron red gold ring glaze ceramic provided by the invention have the following beneficial effects: the fired glaze surface has three characteristics of black base, safflower and gold ring; the glaze safflower is large and controllable in size; the color saturation of the black matrix and the safflower is high; the carthamus tinctorius outer gold ring is clear and visible in thickness.
本发明涉及釉料及陶瓷制备工艺领域，具体涉及一种铁红金圈釉，其特征在于，所述釉料的原料配方以重量份计，包括如下组分：长石42‑46份、高岭土8‑10份、石灰石6‑7份、滑石粉5‑8份、石英12‑14份、骨灰10‑14份、工业铁红粉13‑17份和釉用黄土7‑9份；本发明提供的铁红金圈釉及铁红金圈釉陶瓷的制备工艺具有如下有益效果：烧制的釉面具有黑底、红花、金圈三大特征；釉面红花大且大小可控；黑底和红花的色彩饱和度高；红花外金圈清晰可见且粗细可见。
Iron red gold ring glaze and preparation process of iron red gold ring glaze ceramic
The invention relates to the field of glaze and ceramic preparation processes. The iron oxide red gold ring glaze is characterized in that a raw material formula of the glaze comprises the following components in parts by weight: 42-46 parts of feldspar, 8-10 parts of kaolin, 6-7 parts of limestone, 5-8 parts of talcum powder, 12-14 parts of quartz, 10-14 parts of bone ash, 13-17 parts of industrial iron oxide red powder and 7-9 parts of glaze loess. The iron red gold ring glaze and the preparation process of the iron red gold ring glaze ceramic provided by the invention have the following beneficial effects: the fired glaze surface has three characteristics of black base, safflower and gold ring; the glaze safflower is large and controllable in size; the color saturation of the black matrix and the safflower is high; the carthamus tinctorius outer gold ring is clear and visible in thickness.
本发明涉及釉料及陶瓷制备工艺领域，具体涉及一种铁红金圈釉，其特征在于，所述釉料的原料配方以重量份计，包括如下组分：长石42‑46份、高岭土8‑10份、石灰石6‑7份、滑石粉5‑8份、石英12‑14份、骨灰10‑14份、工业铁红粉13‑17份和釉用黄土7‑9份；本发明提供的铁红金圈釉及铁红金圈釉陶瓷的制备工艺具有如下有益效果：烧制的釉面具有黑底、红花、金圈三大特征；釉面红花大且大小可控；黑底和红花的色彩饱和度高；红花外金圈清晰可见且粗细可见。
Iron red gold ring glaze and preparation process of iron red gold ring glaze ceramic
一种铁红金圈釉及铁红金圈釉陶瓷的制备工艺
LIAO MEIHONG (Autor:in) / ZHENG XIAOFANG (Autor:in)
18.08.2020
Patent
Elektronische Ressource
Chinesisch
Preparation method of matte iron sand gold ceramic glaze
| Europäisches Patentamt | 2020
Lisidian temmoku iron red gold ring crystal glaze and preparation method thereof
| Europäisches Patentamt | 2024
Silver gold ring glaze and preparation method thereof
| Europäisches Patentamt | 2024
Orange red gold ring glaze and preparation method thereof
| Europäisches Patentamt | 2024