Transmutation overglaze and preparation method thereof, and porcelain
The invention discloses a transmutation overglaze. The overglaze comprises the following components in percentage by mass: 70%-75% of frit, 5%-8% of kaolin, 4.5%-6.5% of zinc oxide, 1.2%-2.5% of barium carbonate, 4.5%-6% of titanium dioxide, 2.5%-4.5% of bone meal, 1%-2% of ferric oxide and 1%-2% of cobalt oxide. The invention further discloses a preparation method of the transmutation overglaze and porcelain. According to the transmutation overglaze and the preparation method thereof and the porcelain in the invention, the preparation method of the transmutation overglaze is simple in production process and low in environmental pollution; a unique overglaze formula is adopted, and through mutual cooperation and combined action of all the components and the content of the components, the overglaze is transparent and smooth in surface, good in glaze slip performance and good in firing performance; and an overglaze porcelain product is good in decorative effect, fine and smooth in glazesurface and good in texture. The invention belongs to the technical field of ceramics.
本发明公开了一种窑变釉面釉，所述面釉的组分及各组分的质量百分比为：熔块70%~75%、高岭土5%~8%、氧化锌4.5%~6.5%、碳酸钡1.2%~2.5%、钛白粉4.5%~6%、骨粉2.5%~4.5%、三氧化二铁1%~2%、氧化钴1%~2%。本发明还公开了一种窑变釉面釉制备方法、瓷器。一种窑变釉面釉及其制备方法、瓷器，本窑变釉面釉生产工艺简单，对环境污染少。采用独特的面釉配方，通过各组分及其含量相互配合、共同作用，面釉表面透明光滑、釉浆性能好，烧成性能好；本面釉瓷器制品装饰效果好，釉面细腻，质感良好。本发明适用于陶瓷技术领域。
Transmutation overglaze and preparation method thereof, and porcelain
The invention discloses a transmutation overglaze. The overglaze comprises the following components in percentage by mass: 70%-75% of frit, 5%-8% of kaolin, 4.5%-6.5% of zinc oxide, 1.2%-2.5% of barium carbonate, 4.5%-6% of titanium dioxide, 2.5%-4.5% of bone meal, 1%-2% of ferric oxide and 1%-2% of cobalt oxide. The invention further discloses a preparation method of the transmutation overglaze and porcelain. According to the transmutation overglaze and the preparation method thereof and the porcelain in the invention, the preparation method of the transmutation overglaze is simple in production process and low in environmental pollution; a unique overglaze formula is adopted, and through mutual cooperation and combined action of all the components and the content of the components, the overglaze is transparent and smooth in surface, good in glaze slip performance and good in firing performance; and an overglaze porcelain product is good in decorative effect, fine and smooth in glazesurface and good in texture. The invention belongs to the technical field of ceramics.
本发明公开了一种窑变釉面釉，所述面釉的组分及各组分的质量百分比为：熔块70%~75%、高岭土5%~8%、氧化锌4.5%~6.5%、碳酸钡1.2%~2.5%、钛白粉4.5%~6%、骨粉2.5%~4.5%、三氧化二铁1%~2%、氧化钴1%~2%。本发明还公开了一种窑变釉面釉制备方法、瓷器。一种窑变釉面釉及其制备方法、瓷器，本窑变釉面釉生产工艺简单，对环境污染少。采用独特的面釉配方，通过各组分及其含量相互配合、共同作用，面釉表面透明光滑、釉浆性能好，烧成性能好；本面釉瓷器制品装饰效果好，釉面细腻，质感良好。本发明适用于陶瓷技术领域。
Transmutation overglaze and preparation method thereof, and porcelain
一种窑变釉面釉及其制备方法、瓷器
WU ZUOMING (Autor:in) / WU DAIXUN (Autor:in) / XU TENG (Autor:in) / ZENG LIPENG (Autor:in) / CAI ZHAOJIE (Autor:in)
25.08.2020
Patent
Elektronische Ressource
Chinesisch
| Europäisches Patentamt | 2023
Method for manufacturing peony porcelain based on overglaze color
| Europäisches Patentamt | 2024
Overglaze blue and white porcelain plate painting and manufacturing process thereof
| Europäisches Patentamt | 2023
| Europäisches Patentamt | 2024