Anti-corrosion coating for aluminum-magnesium-silicon sagger
The invention belongs to the technical field of saggers for synthesizing lithium battery cathode materials, and provides an anti-corrosion coating for an aluminum-magnesium-silicon sagger. The anti-corrosion coating for the aluminum-magnesium-silicon sagger is used for directly modifying the surface layer of the aluminum-magnesium-silicon sagger, so that the aluminum-magnesium-silicon sagger has an excellent anti-erosion tissue structure and chemical composition; the anti-corrosion coating comprises the following solid raw materials: 30-70% of alkaline earth metal salt; 20%-40% of TiO2; 2%-10%of SiO2; 5%-10% of Al2O3; 1%-5% of borax; 0.1%-0.3% of a dispersing agent; and 0.3%-10% of a binding agent. The anti-corrosion coating further comprises water, and the addition amount of the water is10-40% of the total weight of the solid raw materials. According to the coating, the surface of the aluminum-magnesium-silicon sagger is modified, so that the aluminum-magnesium-silicon sagger has excellent lithium corrosion resistant chemical composition and structure, meanwhile, the preparation process is simple, low-cost preparation can be realized, and the practical value is achieved.
本发明属于锂电正极材料合成用匣钵技术领域，提出一种铝镁硅质匣钵用防腐蚀涂料。提出的一种铝镁硅质匣钵用防腐蚀涂料用以对铝镁硅质匣钵的表层直接进行改性，使其具备抗侵蚀优异的组织结构和化学组成；所述防腐蚀涂料的固体原料组成为：碱土金属盐 30%～70%；TiO20%～40%；SiO2%～10%；AlO5%～10%；硼砂1%～5%；分散剂0.1%～0.3%；结合剂0.3%～10%；所述防腐蚀涂料还包括有水，水的加入量为上述固体原料总重量的10%～40%。该涂层实现了对铝镁硅质匣钵表面改性，使其具有优异的抗锂侵蚀化学组成以及组织结构，同时制备工艺简单，可实现低成本制备，具有实用价值。
Anti-corrosion coating for aluminum-magnesium-silicon sagger
The invention belongs to the technical field of saggers for synthesizing lithium battery cathode materials, and provides an anti-corrosion coating for an aluminum-magnesium-silicon sagger. The anti-corrosion coating for the aluminum-magnesium-silicon sagger is used for directly modifying the surface layer of the aluminum-magnesium-silicon sagger, so that the aluminum-magnesium-silicon sagger has an excellent anti-erosion tissue structure and chemical composition; the anti-corrosion coating comprises the following solid raw materials: 30-70% of alkaline earth metal salt; 20%-40% of TiO2; 2%-10%of SiO2; 5%-10% of Al2O3; 1%-5% of borax; 0.1%-0.3% of a dispersing agent; and 0.3%-10% of a binding agent. The anti-corrosion coating further comprises water, and the addition amount of the water is10-40% of the total weight of the solid raw materials. According to the coating, the surface of the aluminum-magnesium-silicon sagger is modified, so that the aluminum-magnesium-silicon sagger has excellent lithium corrosion resistant chemical composition and structure, meanwhile, the preparation process is simple, low-cost preparation can be realized, and the practical value is achieved.
本发明属于锂电正极材料合成用匣钵技术领域，提出一种铝镁硅质匣钵用防腐蚀涂料。提出的一种铝镁硅质匣钵用防腐蚀涂料用以对铝镁硅质匣钵的表层直接进行改性，使其具备抗侵蚀优异的组织结构和化学组成；所述防腐蚀涂料的固体原料组成为：碱土金属盐 30%～70%；TiO20%～40%；SiO2%～10%；AlO5%～10%；硼砂1%～5%；分散剂0.1%～0.3%；结合剂0.3%～10%；所述防腐蚀涂料还包括有水，水的加入量为上述固体原料总重量的10%～40%。该涂层实现了对铝镁硅质匣钵表面改性，使其具有优异的抗锂侵蚀化学组成以及组织结构，同时制备工艺简单，可实现低成本制备，具有实用价值。
Anti-corrosion coating for aluminum-magnesium-silicon sagger
一种铝镁硅质匣钵用防腐蚀涂料
QIAN FAN (Autor:in) / LIU GUOQI (Autor:in) / WANG LONGGUANG (Autor:in) / LI HONGXIA (Autor:in) / YANG WENGANG (Autor:in) / YU JIANBIN (Autor:in) / MA WEIKUI (Autor:in)
11.09.2020
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
Silicon carbide coating for sagger and preparation method thereof
| Europäisches Patentamt | 2020
| Europäisches Patentamt | 2022
| Europäisches Patentamt | 2024