The invention relates to a redundant reliability sealing treatment process for building construction joints. The sealing treatment process comprises the following steps: step a, cleaning; step b, slurry preparing, specifically, firstly mixing and stirring powder and a liquid material, then, adding water having the equal mass with the liquid material after uniform stirring, and performing continuous stirring for 10 minutes to obtain slurry, wherein, the powder consists of 8-12 parts of portland cement, 17-23 parts of fine sand and 0.1-0.15 part of strong oxidant in parts by weight, the mass ratio of the liquid material to the powder is 1:10, and the liquid material is polymer emulsion; step c, spraying; and step d, pouring. The invention aims to at least solve the problem that water leakageis prone to occurring in existing building construction joints, and provides the redundant reliability sealing treatment process for the building construction joints.
本发明涉及一种建筑施工缝冗余可靠性密封处理工艺，所述包括如下步骤：步骤a，清洗；步骤b，制浆；先将粉料和液料混合搅拌，待搅拌均匀后再加入和液料等质量的水，继续搅拌10分钟，得到浆料；其中，所述粉料按质量份数计，组成为：硅酸盐水泥：8~12份；细沙：17~23份；强氧化剂：0.1~0.15份；其中，所述液料与粉料的质量比为1：10，液料为聚合物乳液；步骤c，喷涂；步骤d，浇筑。本发明的目的在于解决或至少现有建筑施工缝易漏水的问题，提供一种建筑施工缝冗余可靠性密封处理工艺。
Redundant reliability sealing treatment process for building construction joints
The invention relates to a redundant reliability sealing treatment process for building construction joints. The sealing treatment process comprises the following steps: step a, cleaning; step b, slurry preparing, specifically, firstly mixing and stirring powder and a liquid material, then, adding water having the equal mass with the liquid material after uniform stirring, and performing continuous stirring for 10 minutes to obtain slurry, wherein, the powder consists of 8-12 parts of portland cement, 17-23 parts of fine sand and 0.1-0.15 part of strong oxidant in parts by weight, the mass ratio of the liquid material to the powder is 1:10, and the liquid material is polymer emulsion; step c, spraying; and step d, pouring. The invention aims to at least solve the problem that water leakageis prone to occurring in existing building construction joints, and provides the redundant reliability sealing treatment process for the building construction joints.
本发明涉及一种建筑施工缝冗余可靠性密封处理工艺，所述包括如下步骤：步骤a，清洗；步骤b，制浆；先将粉料和液料混合搅拌，待搅拌均匀后再加入和液料等质量的水，继续搅拌10分钟，得到浆料；其中，所述粉料按质量份数计，组成为：硅酸盐水泥：8~12份；细沙：17~23份；强氧化剂：0.1~0.15份；其中，所述液料与粉料的质量比为1：10，液料为聚合物乳液；步骤c，喷涂；步骤d，浇筑。本发明的目的在于解决或至少现有建筑施工缝易漏水的问题，提供一种建筑施工缝冗余可靠性密封处理工艺。
Redundant reliability sealing treatment process for building construction joints
一种建筑施工缝冗余可靠性密封处理工艺