Eine Plattform für die Wissenschaft: Bauingenieurwesen, Architektur und Urbanistik
Eine Plattform für die Wissenschaft: Bauingenieurwesen, Architektur und Urbanistik
The invention discloses a firing process of Yinhao Jianzhan. The firing process comprises the following steps of: S1, blank selection; S2, primary temperature control; S3, secondary temperature control; S4, firing and forming; S5, oil firewood adding: performing heating to 1000-1050DEG C in an electric kiln, keeping the temperature constant for 4-5h, adding 300-350g of oil firewood, adding 180-250g of oil firewood every 10-12min, adding the oil firewood for 6-8 times in total, performing natural cooling after the temperature is constant, and performing discharging to obtain the Yinhao Jianzhan. According to the Yinhao Jianzhan fired by the firing method provided by the invention, blank selection and multiple times of temperature control work are carried out to lower the temperature rise rate, meanwhile, the temperature in the firing kiln is continuously detected, the heating temperature is controlled according to the temperature change in the kiln, the number of glaze shrinkage pointsand glaze wrap angles after firing of the Yinhao Jianzhan is reduced, the success rate of the Yinhao Jianzhan is greatly increased, resource waste is reduced, meanwhile, an automatic gas supply bottlepouring mode is adopted, energy consumed by manual gas supply bottle pouring is reduced, and time and labor are saved.
本发明公开了一种银毫建盏的烧制工艺，包括以下步骤：S1、选胚；S2、初次控温；S3、二次控温；S4、烧制成型；S5、投入油柴：在电窑炉内温度加热至1000‑1050℃，恒温4‑5h后，投入300‑350g油柴，之后每间隔10‑12min，投入180‑250g油柴，共投入油柴次数6‑8次，恒温完毕后，自然冷却出炉，得到银毫建盏；采用本发明银毫建盏烧制方法烧制出的银毫建盏，经过选胚、多次控温工作，降低升温速度，同时，不断检测烧制窑内温度，根据窑内温度变化，控制加热温度，减小了银毫建盏烧制完毕后出现缩釉点、釉包角数量，极大的提高了银毫建盏良品的成功率，减小了资源的浪费，同时，本发明采用自动浇灌供气瓶的方式，减小了人力浇灌供气瓶所耗费的精力，省时省力。
The invention discloses a firing process of Yinhao Jianzhan. The firing process comprises the following steps of: S1, blank selection; S2, primary temperature control; S3, secondary temperature control; S4, firing and forming; S5, oil firewood adding: performing heating to 1000-1050DEG C in an electric kiln, keeping the temperature constant for 4-5h, adding 300-350g of oil firewood, adding 180-250g of oil firewood every 10-12min, adding the oil firewood for 6-8 times in total, performing natural cooling after the temperature is constant, and performing discharging to obtain the Yinhao Jianzhan. According to the Yinhao Jianzhan fired by the firing method provided by the invention, blank selection and multiple times of temperature control work are carried out to lower the temperature rise rate, meanwhile, the temperature in the firing kiln is continuously detected, the heating temperature is controlled according to the temperature change in the kiln, the number of glaze shrinkage pointsand glaze wrap angles after firing of the Yinhao Jianzhan is reduced, the success rate of the Yinhao Jianzhan is greatly increased, resource waste is reduced, meanwhile, an automatic gas supply bottlepouring mode is adopted, energy consumed by manual gas supply bottle pouring is reduced, and time and labor are saved.
本发明公开了一种银毫建盏的烧制工艺，包括以下步骤：S1、选胚；S2、初次控温；S3、二次控温；S4、烧制成型；S5、投入油柴：在电窑炉内温度加热至1000‑1050℃，恒温4‑5h后，投入300‑350g油柴，之后每间隔10‑12min，投入180‑250g油柴，共投入油柴次数6‑8次，恒温完毕后，自然冷却出炉，得到银毫建盏；采用本发明银毫建盏烧制方法烧制出的银毫建盏，经过选胚、多次控温工作，降低升温速度，同时，不断检测烧制窑内温度，根据窑内温度变化，控制加热温度，减小了银毫建盏烧制完毕后出现缩釉点、釉包角数量，极大的提高了银毫建盏良品的成功率，减小了资源的浪费，同时，本发明采用自动浇灌供气瓶的方式，减小了人力浇灌供气瓶所耗费的精力，省时省力。