The invention discloses a ceramic firing method. The method comprises the following steps of: (1) preparing red clay; (2) batching, namely selecting 60-85 parts by weight of the red glue soil preparedin the step (1), 5-10 parts by weight of quartz and 15-20 parts by weight of feldspar, and uniformly mixing the raw materials for later use; (3) carrying out slurry preparation, namely adding 0.4-0.6parts by weight of water into each part by weight of the mixed raw materials, and then putting the mixture into a ball mill and grinding the mixture into 310-350-mesh slurry; (4) preparing a potteryblank, and naturally drying the pottery blank in the shade until the water content is less than 6%; and (3) firing, namely performing primary firing shaping and secondary firing to obtain colorless unglazed black pottery. The invention belongs to the technical field of ceramic firing, and particularly relates to a ceramic firing method for preparing a black pottery product by fully utilizing red clay.
本发明公开了一种陶瓷烧制方法，包括如下步骤：1)红胶土制备；2)配料，按重量份数选取步骤1制得的红胶土60‑85份，石英5‑10份，长石15‑20份，混合均匀备用；3)浆料制备，将混合好的原料按重量比重每份原料加入0.4‑0.6份水，然后放入球磨机研磨成310‑350目的浆料；4)制坯，并将陶坯自然阴干到含水量6％以下；5)烧制，经过一次烧制定型，二次烧制，即可得到无色无釉的黑陶。本发明属于陶瓷烧制技术领域，具体是指一种充分利用红胶土制备黑陶制品的陶瓷烧制方法。
The invention discloses a ceramic firing method. The method comprises the following steps of: (1) preparing red clay; (2) batching, namely selecting 60-85 parts by weight of the red glue soil preparedin the step (1), 5-10 parts by weight of quartz and 15-20 parts by weight of feldspar, and uniformly mixing the raw materials for later use; (3) carrying out slurry preparation, namely adding 0.4-0.6parts by weight of water into each part by weight of the mixed raw materials, and then putting the mixture into a ball mill and grinding the mixture into 310-350-mesh slurry; (4) preparing a potteryblank, and naturally drying the pottery blank in the shade until the water content is less than 6%; and (3) firing, namely performing primary firing shaping and secondary firing to obtain colorless unglazed black pottery. The invention belongs to the technical field of ceramic firing, and particularly relates to a ceramic firing method for preparing a black pottery product by fully utilizing red clay.
本发明公开了一种陶瓷烧制方法，包括如下步骤：1)红胶土制备；2)配料，按重量份数选取步骤1制得的红胶土60‑85份，石英5‑10份，长石15‑20份，混合均匀备用；3)浆料制备，将混合好的原料按重量比重每份原料加入0.4‑0.6份水，然后放入球磨机研磨成310‑350目的浆料；4)制坯，并将陶坯自然阴干到含水量6％以下；5)烧制，经过一次烧制定型，二次烧制，即可得到无色无釉的黑陶。本发明属于陶瓷烧制技术领域，具体是指一种充分利用红胶土制备黑陶制品的陶瓷烧制方法。
Ceramic firing method
一种陶瓷烧制方法