Dark green transmutation glaze ceramic product and preparation method thereof
The invention relates to the technical field of ceramic preparation, and concretely relates to a dark green transmutation glaze ceramic product and a preparation method thereof. The dark green transmutation glaze ceramic product is prepared from, by weight, 64-72 parts of kaolin, 40-45 parts of glass powder, 6-10 parts of talc, 10-12 parts of quartz, 4-9 parts of calcium carbonate, 3-5 parts of ferric oxide, 3-8 parts of copper oxide, 1-3 parts of chrome green and 1-2 parts of phosphorus pentoxide. The preparation method comprises the following steps: S1, glaze preparation; S2, slurry preparation; S3, glazing; and S4, sintering. The ceramic product has the characteristics of bright color, uniform and clear texture, wear resistance and scratch resistance.
本发明涉及陶瓷制备技术领域，具体为一种墨绿色窑变釉陶瓷制品及其制备方法。所述墨绿色窑变釉陶瓷制品，包括以下重量份的原料：高岭土64‑72份、玻璃粉40‑45份、滑石6‑10份、石英10‑12份、碳酸钙4‑9份、氧化铁3‑5份、氧化铜3‑8份、铬绿1‑3份、五氧化二磷1‑2份。其制备方法的步骤为：S1釉料配备、S2泥浆制备、S3施釉、S4烧成。本发明陶瓷制品具有色泽艳丽、纹理均匀清晰以及耐磨抗刮的特点。
Dark green transmutation glaze ceramic product and preparation method thereof
The invention relates to the technical field of ceramic preparation, and concretely relates to a dark green transmutation glaze ceramic product and a preparation method thereof. The dark green transmutation glaze ceramic product is prepared from, by weight, 64-72 parts of kaolin, 40-45 parts of glass powder, 6-10 parts of talc, 10-12 parts of quartz, 4-9 parts of calcium carbonate, 3-5 parts of ferric oxide, 3-8 parts of copper oxide, 1-3 parts of chrome green and 1-2 parts of phosphorus pentoxide. The preparation method comprises the following steps: S1, glaze preparation; S2, slurry preparation; S3, glazing; and S4, sintering. The ceramic product has the characteristics of bright color, uniform and clear texture, wear resistance and scratch resistance.
本发明涉及陶瓷制备技术领域，具体为一种墨绿色窑变釉陶瓷制品及其制备方法。所述墨绿色窑变釉陶瓷制品，包括以下重量份的原料：高岭土64‑72份、玻璃粉40‑45份、滑石6‑10份、石英10‑12份、碳酸钙4‑9份、氧化铁3‑5份、氧化铜3‑8份、铬绿1‑3份、五氧化二磷1‑2份。其制备方法的步骤为：S1釉料配备、S2泥浆制备、S3施釉、S4烧成。本发明陶瓷制品具有色泽艳丽、纹理均匀清晰以及耐磨抗刮的特点。
Dark green transmutation glaze ceramic product and preparation method thereof
一种墨绿色窑变釉陶瓷制品及其制备方法
XU CHANGYI (Autor:in)
04.12.2020
Patent
Elektronische Ressource
Chinesisch
Transmutation glaze, transmutation glaze laterite ceramic product and preparation method thereof
| Europäisches Patentamt | 2022
| Europäisches Patentamt | 2022
| Europäisches Patentamt | 2016
| Europäisches Patentamt | 2024