Manufacturing method and application of composite zirconium-titanium opacified frit
The invention discloses a manufacturing method and application of a composite zirconium-titanium opacified frit. The manufacturing method comprises the following steps of: accurately weighing variousmineral raw materials and chemical materials according to the oxide composition set in the formula, uniformly mixing the mineral raw materials and the chemical materials, continuously and uniformly adding the mixed glass batch into a glass melting furnace, melting at 1560 DEG C to obtain transparent molten glass, and quenching the molten glass in cold water to obtain yellow frit particles. The frit particles are introduced into a ceramic glaze formula, part of zirconium silicate is replaced according to the proportion of 2: 1, the whiteness of a ceramic glaze surface can be remarkably improved, the use amount of an expensive glaze whitening agent zirconium silicate can be reduced, and the cost of the ceramic glaze is greatly reduced.
本发明公开了一种复合锆钛乳浊熔块的制造方法及应用，首先按照配方设定的氧化物组成将各种矿物原料及化工料进行准确的称量，然后混合均匀，将混合好的玻璃配合料连续均匀的投入玻璃熔化炉，在1560度高温下熔化成透明的玻璃液，然后将玻璃液在冷水中水淬，得到黄色的熔块颗粒。将这种熔块颗粒引入到陶瓷釉料配方中，按照2：1的比例替换一部分硅酸锆，可以显著的提高陶瓷釉面的白度，还可以降低价格高昂的釉料增白剂硅酸锆的用量，大幅度降低陶瓷釉料的成本。
Manufacturing method and application of composite zirconium-titanium opacified frit
The invention discloses a manufacturing method and application of a composite zirconium-titanium opacified frit. The manufacturing method comprises the following steps of: accurately weighing variousmineral raw materials and chemical materials according to the oxide composition set in the formula, uniformly mixing the mineral raw materials and the chemical materials, continuously and uniformly adding the mixed glass batch into a glass melting furnace, melting at 1560 DEG C to obtain transparent molten glass, and quenching the molten glass in cold water to obtain yellow frit particles. The frit particles are introduced into a ceramic glaze formula, part of zirconium silicate is replaced according to the proportion of 2: 1, the whiteness of a ceramic glaze surface can be remarkably improved, the use amount of an expensive glaze whitening agent zirconium silicate can be reduced, and the cost of the ceramic glaze is greatly reduced.
本发明公开了一种复合锆钛乳浊熔块的制造方法及应用，首先按照配方设定的氧化物组成将各种矿物原料及化工料进行准确的称量，然后混合均匀，将混合好的玻璃配合料连续均匀的投入玻璃熔化炉，在1560度高温下熔化成透明的玻璃液，然后将玻璃液在冷水中水淬，得到黄色的熔块颗粒。将这种熔块颗粒引入到陶瓷釉料配方中，按照2：1的比例替换一部分硅酸锆，可以显著的提高陶瓷釉面的白度，还可以降低价格高昂的釉料增白剂硅酸锆的用量，大幅度降低陶瓷釉料的成本。
Manufacturing method and application of composite zirconium-titanium opacified frit
一种复合锆钛乳浊熔块的制造方法及应用
ZUO MING (Autor:in) / ZHAO XIAOPING (Autor:in)
11.12.2020
Patent
Elektronische Ressource
Chinesisch
| Europäisches Patentamt | 2023
| Europäisches Patentamt | 2021
| Europäisches Patentamt | 2024
Ceramic tile, frit for manufacturing ceramic tile and preparation method of frit
| Europäisches Patentamt | 2020
| Europäisches Patentamt | 2021