Anti-sticking agent for improving turnover rate of slag ladle, and preparation method thereof
The invention discloses an anti-sticking agent capable of increasing the slag ladle turnover rate, and a preparation method of the anti-sticking agent. The anti-sticking agent comprises the followingcomponents in parts by weight: 10-15 parts of lime, 40-50 parts of dolomite, 30-40 parts of waste magnesia carbon bricks, 1-3 parts of bentonite, 10-20 parts of talcum powder, 15-20 parts of quartz, 1-5 parts of a curing agent and 1-5 parts of a coagulant. The preparation method of the anti-sticking agent comprises the following steps: (1) uniformly mixing lime and dolomite in a weight ratio of 1:(1-2) according to a formula, and pressing into balls to obtain an anti-sticking material A; and (2) mixing the rest dolomite, waste magnesia carbon bricks, bentonite, talcum powder, quartz, a curingagent and a coagulant according to the formula, adding water, and uniformly stirring to obtain the anti-sticking material B matched with the anti-sticking material A. The anti-sticking agent preparedby the invention can effectively prevent the slag ladle from sticking, prolong the service life of the slag ladle and reduce the production cost.
本发明公开了一种提高渣罐脱翻率的防粘剂及其制备方法。该防粘剂，包括以下重量份的组分：白灰10～15份、白云石40～50份、废镁碳砖30～40份、膨润土1～3份、滑石粉10～20份、石英15～20份、固化剂1～5份，以及促凝剂1～5份；该防粘剂的制备方法，包括以下步骤：(1)按配方将白灰与白云石以重量比为1:1～2的比例混合均匀后压球，得防粘材料A；(2)按配方将剩余的白云石、废镁碳砖、膨润土、滑石粉、石英、固化剂，以及促凝剂混合后，加水搅拌均匀，得与防粘材料A配合使用的防粘材料B。本发明制备得到的防粘剂可以有效防止渣罐粘，延长渣罐的使用寿命，降低生产成本。
Anti-sticking agent for improving turnover rate of slag ladle, and preparation method thereof
The invention discloses an anti-sticking agent capable of increasing the slag ladle turnover rate, and a preparation method of the anti-sticking agent. The anti-sticking agent comprises the followingcomponents in parts by weight: 10-15 parts of lime, 40-50 parts of dolomite, 30-40 parts of waste magnesia carbon bricks, 1-3 parts of bentonite, 10-20 parts of talcum powder, 15-20 parts of quartz, 1-5 parts of a curing agent and 1-5 parts of a coagulant. The preparation method of the anti-sticking agent comprises the following steps: (1) uniformly mixing lime and dolomite in a weight ratio of 1:(1-2) according to a formula, and pressing into balls to obtain an anti-sticking material A; and (2) mixing the rest dolomite, waste magnesia carbon bricks, bentonite, talcum powder, quartz, a curingagent and a coagulant according to the formula, adding water, and uniformly stirring to obtain the anti-sticking material B matched with the anti-sticking material A. The anti-sticking agent preparedby the invention can effectively prevent the slag ladle from sticking, prolong the service life of the slag ladle and reduce the production cost.
本发明公开了一种提高渣罐脱翻率的防粘剂及其制备方法。该防粘剂，包括以下重量份的组分：白灰10～15份、白云石40～50份、废镁碳砖30～40份、膨润土1～3份、滑石粉10～20份、石英15～20份、固化剂1～5份，以及促凝剂1～5份；该防粘剂的制备方法，包括以下步骤：(1)按配方将白灰与白云石以重量比为1:1～2的比例混合均匀后压球，得防粘材料A；(2)按配方将剩余的白云石、废镁碳砖、膨润土、滑石粉、石英、固化剂，以及促凝剂混合后，加水搅拌均匀，得与防粘材料A配合使用的防粘材料B。本发明制备得到的防粘剂可以有效防止渣罐粘，延长渣罐的使用寿命，降低生产成本。
Anti-sticking agent for improving turnover rate of slag ladle, and preparation method thereof
一种提高渣罐脱翻率的防粘剂及其制备方法
FAN ZEYU (Autor:in) / QIAN QIANG (Autor:in) / YANG JINYU (Autor:in) / ZHANG RUYUAN (Autor:in) / SONG WENDE (Autor:in)
12.02.2021
Patent
Elektronische Ressource
Chinesisch
Formula and manufacturing method of slag ladle trunnion anti-sticking steel sheath
| Europäisches Patentamt | 2021
Novel anti-sticking spray coating for high-titanium blast furnace slag ladle
| Europäisches Patentamt | 2023
Ladle slag adhesion preventing agent and using method thereof
| Europäisches Patentamt | 2021
Efficient concrete anti-sticking agent and preparation method thereof
| Europäisches Patentamt | 2023