Preparation method of nitride-combined silicon carbide wear-resistant ceramic part for slurry pump
The invention relates to a preparation process of a wear-resistant and refractory material, and provides a preparation method of a nitride-combined silicon carbide wear-resistant ceramic part for a slurry pump. According to the preparation method of the nitride-combined silicon carbide wear-resistant ceramic part for the slurry pump, silicon carbide is used as a main raw material, modified metal silicon powder of which D50 is smaller than 0.5 [mu] m; the addition amount ratio of the modified metal silicon powder to the silicon carbide is 1-10%: 90%-99%; and the modified metal silicon powder, the silicon carbide, a binding agent and water are mixed so as to form a castable, the castable is injected into a mold, vibration casting molding is carried out, and curing, drying, and sintering are performed to obtain the product. The energy-saving and consumption-reducing effects of the ceramic part are obvious; the high abrasion resistance of the material is achieved to the maximum extent; the full-life-cycle service capacity of the nitride-combined silicon carbide wear-resistant ceramic part for the slurry pump is improved; and the nitride-combined silicon carbide wear-resistant ceramic part for the slurry pump is sintered at high temperature and is not limited by the temperature of a use environment.
本发明涉及耐磨、耐火材料制备工艺,提供一种渣浆泵用氮化物结合碳化硅耐磨陶瓷件的制备方法。一种渣浆泵用氮化物结合碳化硅耐磨陶瓷件的制备方法以碳化硅为主要原料,并引入D50<0.5μm改性金属硅粉;改性金属硅粉与碳化硅的加入量为1~10%:90%~99%;与结合剂和水混成浇注料后,注入模具振动浇注成型,经养护、烘干后烧成制得制品。本发明节能降耗效果明显,最大限度实现材料本身的高耐磨性,提高渣浆泵用氮化物结合碳化硅耐磨陶瓷件的全生命周期服役能力;该渣浆泵用氮化物结合碳化硅耐磨陶瓷件经过高温烧成,不受使用环境温度的限制。
Preparation method of nitride-combined silicon carbide wear-resistant ceramic part for slurry pump
The invention relates to a preparation process of a wear-resistant and refractory material, and provides a preparation method of a nitride-combined silicon carbide wear-resistant ceramic part for a slurry pump. According to the preparation method of the nitride-combined silicon carbide wear-resistant ceramic part for the slurry pump, silicon carbide is used as a main raw material, modified metal silicon powder of which D50 is smaller than 0.5 [mu] m; the addition amount ratio of the modified metal silicon powder to the silicon carbide is 1-10%: 90%-99%; and the modified metal silicon powder, the silicon carbide, a binding agent and water are mixed so as to form a castable, the castable is injected into a mold, vibration casting molding is carried out, and curing, drying, and sintering are performed to obtain the product. The energy-saving and consumption-reducing effects of the ceramic part are obvious; the high abrasion resistance of the material is achieved to the maximum extent; the full-life-cycle service capacity of the nitride-combined silicon carbide wear-resistant ceramic part for the slurry pump is improved; and the nitride-combined silicon carbide wear-resistant ceramic part for the slurry pump is sintered at high temperature and is not limited by the temperature of a use environment.
本发明涉及耐磨、耐火材料制备工艺,提供一种渣浆泵用氮化物结合碳化硅耐磨陶瓷件的制备方法。一种渣浆泵用氮化物结合碳化硅耐磨陶瓷件的制备方法以碳化硅为主要原料,并引入D50<0.5μm改性金属硅粉;改性金属硅粉与碳化硅的加入量为1~10%:90%~99%;与结合剂和水混成浇注料后,注入模具振动浇注成型,经养护、烘干后烧成制得制品。本发明节能降耗效果明显,最大限度实现材料本身的高耐磨性,提高渣浆泵用氮化物结合碳化硅耐磨陶瓷件的全生命周期服役能力;该渣浆泵用氮化物结合碳化硅耐磨陶瓷件经过高温烧成,不受使用环境温度的限制。
Preparation method of nitride-combined silicon carbide wear-resistant ceramic part for slurry pump
一种渣浆泵用氮化物结合碳化硅耐磨陶瓷件的制备方法
CAO HUIYAN (Autor:in) / LYU CHUNJIANG (Autor:in) / HUANG YIFEI (Autor:in) / FENG YANBIN (Autor:in) / CHENG ZHU (Autor:in) / WANG WENWU (Autor:in) / LI JIE (Autor:in) / LIU YUN (Autor:in) / WANG YONG (Autor:in) / MA SHAOYANG (Autor:in)
20.04.2021
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
Europäisches Patentamt | 2023
|Europäisches Patentamt | 2021
|Europäisches Patentamt | 2024
|Europäisches Patentamt | 2024
|SILICON NITRIDE, CERAMIC SLURRY AND PREPARATION METHOD
Europäisches Patentamt | 2022
|