The invention belongs to the technical field of ceramic glaze preparation, and particularly relates to a crackle glaze and a preparation method thereof, the crackle glaze comprises the following components by weight: 5-15 parts of quartz, 10-25 parts of calcite, 5-10 parts of kaolin, 20-40 parts of high-calcium low-aluminum frit, 20-70 parts of barium carbonate, 3-15 parts of dolomite, 10-40 parts of albite, and 1-5 parts of burnt zinc; and the production cost is low, the firing range is wide, the glaze slip is not prone to sinking to the bottom and hardening, and the thermal shock resistance and the large piece yield are obviously improved.
本发明属于一种陶瓷釉料制备技术领域,具体是涉及到一种裂纹釉和制备方法,包括如下重量份的组分:石英5‑15份,方解石10‑25份,高岭土5‑10份,高钙低铝熔块20‑40份,碳酸钡20‑70份,白云石3‑15份,钠长石10‑40份,烧锌1‑5份;本申请生产成本低,烧成范围广,且釉浆不易沉底,不易板结,抗热震性能和大件良品率明显提高。
The invention belongs to the technical field of ceramic glaze preparation, and particularly relates to a crackle glaze and a preparation method thereof, the crackle glaze comprises the following components by weight: 5-15 parts of quartz, 10-25 parts of calcite, 5-10 parts of kaolin, 20-40 parts of high-calcium low-aluminum frit, 20-70 parts of barium carbonate, 3-15 parts of dolomite, 10-40 parts of albite, and 1-5 parts of burnt zinc; and the production cost is low, the firing range is wide, the glaze slip is not prone to sinking to the bottom and hardening, and the thermal shock resistance and the large piece yield are obviously improved.
本发明属于一种陶瓷釉料制备技术领域,具体是涉及到一种裂纹釉和制备方法,包括如下重量份的组分:石英5‑15份,方解石10‑25份,高岭土5‑10份,高钙低铝熔块20‑40份,碳酸钡20‑70份,白云石3‑15份,钠长石10‑40份,烧锌1‑5份;本申请生产成本低,烧成范围广,且釉浆不易沉底,不易板结,抗热震性能和大件良品率明显提高。
Cracked glaze and preparation method thereof
一种裂纹釉和制备方法
07.05.2021
Patent
Elektronische Ressource
Chinesisch
Cracked glaze, preparation method thereof and sanitary ceramic containing cracked glaze