Golden Grignard metal glaze and processing technology thereof
The invention discloses a golden Grignard metal glaze and a processing technology thereof. The formula comprises ultra-white washing mud, lithiated silicon micropowder, frit, albite, ferric oxide, a color developing agent, tin oxide, zinc oxide and copper oxide. The mass percentage content of each component is as follows: 5-10% of ultra-white washing mud, 1-3% of lithiated silicon micropowder, 20-40% of frit, 30-40% of albite, 10-20% of ferric oxide, 5-10% of a color developing agent, 1-5% of tin oxide, 1-3% of zinc oxide and 1-3% of copper oxide. The processing technology comprises the following steps: step 1, material selection; step 2, mixing treatment; step 3, glaze slip detection; step 4, kiln loading and firing; and step 5, storing and placing. The glaze has rich colors, strong metal texture, mottle rheology or gulch-like flickering effect, soft glaze gloss and smooth and fine hand feeling; and the Grignard metal glaze can be combined and matched with other glazes or used independently, can also be used as silk-screen printing glaze and mouth edge glaze, and has very ideal decoration and embellishment effects.
本发明公开了一种金黄格氏金属釉及其加工工艺，配方包括：超白洗泥、岩化硅微粉、熔块、钠长石、氧化铁、显色剂、氧化锡、氧化锌和氧化铜，各组分的质量百分含量分别是：5‑10%的超白洗泥、1‑3%的岩化硅微粉、20‑40%的熔块、30‑40%的钠长石、10‑20%的氧化铁、5‑10%的显色剂、1‑5%的氧化锡、1‑3%的氧化锌和1‑3%的氧化铜；包括以下步骤，步骤一，材料选取；步骤二，混合处理；步骤三，釉浆检测；步骤四，装窑烧成；步骤五，存储放置；该发明，具有丰富的色彩、强烈的金属质感、斑驳流变或砂金般闪烁的效果、柔和的釉面光泽、平滑细腻的手感；格氏金属釉可与其他釉料组合搭配或单独使用，亦可以作为丝网印刷釉、口沿釉使用，具有十分理想的装饰点缀效果。
Golden Grignard metal glaze and processing technology thereof
The invention discloses a golden Grignard metal glaze and a processing technology thereof. The formula comprises ultra-white washing mud, lithiated silicon micropowder, frit, albite, ferric oxide, a color developing agent, tin oxide, zinc oxide and copper oxide. The mass percentage content of each component is as follows: 5-10% of ultra-white washing mud, 1-3% of lithiated silicon micropowder, 20-40% of frit, 30-40% of albite, 10-20% of ferric oxide, 5-10% of a color developing agent, 1-5% of tin oxide, 1-3% of zinc oxide and 1-3% of copper oxide. The processing technology comprises the following steps: step 1, material selection; step 2, mixing treatment; step 3, glaze slip detection; step 4, kiln loading and firing; and step 5, storing and placing. The glaze has rich colors, strong metal texture, mottle rheology or gulch-like flickering effect, soft glaze gloss and smooth and fine hand feeling; and the Grignard metal glaze can be combined and matched with other glazes or used independently, can also be used as silk-screen printing glaze and mouth edge glaze, and has very ideal decoration and embellishment effects.
本发明公开了一种金黄格氏金属釉及其加工工艺，配方包括：超白洗泥、岩化硅微粉、熔块、钠长石、氧化铁、显色剂、氧化锡、氧化锌和氧化铜，各组分的质量百分含量分别是：5‑10%的超白洗泥、1‑3%的岩化硅微粉、20‑40%的熔块、30‑40%的钠长石、10‑20%的氧化铁、5‑10%的显色剂、1‑5%的氧化锡、1‑3%的氧化锌和1‑3%的氧化铜；包括以下步骤，步骤一，材料选取；步骤二，混合处理；步骤三，釉浆检测；步骤四，装窑烧成；步骤五，存储放置；该发明，具有丰富的色彩、强烈的金属质感、斑驳流变或砂金般闪烁的效果、柔和的釉面光泽、平滑细腻的手感；格氏金属釉可与其他釉料组合搭配或单独使用，亦可以作为丝网印刷釉、口沿釉使用，具有十分理想的装饰点缀效果。
Golden Grignard metal glaze and processing technology thereof
一种金黄格氏金属釉及其加工工艺
WANG LIANG (Autor:in)
25.05.2021
Patent
Elektronische Ressource
Chinesisch
| Europäisches Patentamt | 2021
Purplish red oxidation Grignard metal glaze and processing technology thereof
| Europäisches Patentamt | 2021
Golden-wire red glaze, ceramic product with golden red glaze and preparation method thereof
| Europäisches Patentamt | 2020
Processing technology for rapidly firing golden flower-shaped crystal metal effect decorative glaze
| Europäisches Patentamt | 2022