Alkali-activated cementing material doped with high-silicon iron tailings and lime and preparation method of alkali-activated cementing material
The invention relates to an alkali-activated cementing material doped with high-silicon iron tailings and lime, which belongs to the field of alkali-activated inorganic nonmetal cementing materials. The invention relates to an alkali-activated cementing material doped with high-silicon iron tailings and lime. The alkali-activated cementing material is prepared from the following raw materials: high-silicon iron tailings, lime, alkaline residues, blast furnace slag and an alkali activator. The raw materials comprise, by mass, 30-50 parts of high-silicon iron tailings, 15-20 parts of lime, 20-40 parts of blast furnace slag, 5-10 parts of alkaline residues, and 1-5 parts of an alkaline activator; and the alkali activator is a solution prepared by mixing NaOH and Na2SiO3. According to the alkali-activated cementing material doped with the high-silicon iron tailings and the lime, the solid waste and the lime generated after mining of an iron ore plant are mainly utilized, the purpose of the alkali-activated cementing material can be achieved by doping a proper amount of the high-silicon iron tailings and the lime, and secondary utilization of the high-silicon iron tailings is achieved.
本发明涉及一种掺高硅型铁尾矿、石灰的碱激发胶凝材料，本发明属于碱激发无机非金属胶凝材料领域。一种掺高硅型铁尾矿、石灰的碱激发胶凝材料，由下述原料制得：高硅型铁尾矿、石灰、碱渣、高炉矿渣、碱性激发剂。质量份原料组成：30~50份高硅型铁尾矿，15~20份石灰，20~40份高炉矿渣、5~10份碱渣，1~5份碱性激发剂；碱激发剂为:NaOH与Na2SiO3混合配制溶液；本发明掺高硅型铁尾矿、石灰的碱激发胶凝材料主要利用铁矿厂开采之后产生的的固体废料和石灰，可通过掺合适量高硅型铁尾矿、石灰达到碱激发胶凝材料的目的，将高硅型铁尾矿二次利用。
Alkali-activated cementing material doped with high-silicon iron tailings and lime and preparation method of alkali-activated cementing material
The invention relates to an alkali-activated cementing material doped with high-silicon iron tailings and lime, which belongs to the field of alkali-activated inorganic nonmetal cementing materials. The invention relates to an alkali-activated cementing material doped with high-silicon iron tailings and lime. The alkali-activated cementing material is prepared from the following raw materials: high-silicon iron tailings, lime, alkaline residues, blast furnace slag and an alkali activator. The raw materials comprise, by mass, 30-50 parts of high-silicon iron tailings, 15-20 parts of lime, 20-40 parts of blast furnace slag, 5-10 parts of alkaline residues, and 1-5 parts of an alkaline activator; and the alkali activator is a solution prepared by mixing NaOH and Na2SiO3. According to the alkali-activated cementing material doped with the high-silicon iron tailings and the lime, the solid waste and the lime generated after mining of an iron ore plant are mainly utilized, the purpose of the alkali-activated cementing material can be achieved by doping a proper amount of the high-silicon iron tailings and the lime, and secondary utilization of the high-silicon iron tailings is achieved.
本发明涉及一种掺高硅型铁尾矿、石灰的碱激发胶凝材料，本发明属于碱激发无机非金属胶凝材料领域。一种掺高硅型铁尾矿、石灰的碱激发胶凝材料，由下述原料制得：高硅型铁尾矿、石灰、碱渣、高炉矿渣、碱性激发剂。质量份原料组成：30~50份高硅型铁尾矿，15~20份石灰，20~40份高炉矿渣、5~10份碱渣，1~5份碱性激发剂；碱激发剂为:NaOH与Na2SiO3混合配制溶液；本发明掺高硅型铁尾矿、石灰的碱激发胶凝材料主要利用铁矿厂开采之后产生的的固体废料和石灰，可通过掺合适量高硅型铁尾矿、石灰达到碱激发胶凝材料的目的，将高硅型铁尾矿二次利用。
Alkali-activated cementing material doped with high-silicon iron tailings and lime and preparation method of alkali-activated cementing material
一种掺高硅型铁尾矿、石灰的碱激发胶凝材料及其制备方法
GU XIAOWEI (Autor:in) / HU ZIYANG (Autor:in) / LIU PENG (Autor:in) / ZOU MINGXIN (Autor:in) / CHI HAOFENG (Autor:in) / WANG SHINING (Autor:in)
25.05.2021
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
| Europäisches Patentamt | 2021
| Europäisches Patentamt | 2022
| Europäisches Patentamt | 2023
Alkali-activated cementing material and preparation method thereof
| Europäisches Patentamt | 2024